1) self-fluxing alloy powder
自熔剂合金粉末
2) self-fluxed alloy powder
自熔性合金粉末
1.
Structure and properties of spray layer made by different quantities of self-fluxed alloy powder are studied.
采用铝热自蔓延高温合成法在钢板表面进行喷焊,研究不同用量自熔性合金粉末所制得的喷焊层的组织及性能,分析了合金元素对基体组织和性能的影响。
3) self fluxing alloyed composite powder
自熔合金粉末
1.
Abrasion wear resistance test of coatings was carried out by using hardened steel45 as an abrasion wear taster Oil the coatings of typical China--made self fluxing alloyed composite powders.
用几种国产自熔合金粉末制备喷熔层与４５淬火钢配对构成摩擦副，进行摩擦磨损试验，以相对磨损量评价喷熔层的摩擦磨损性能。
4) self molten Fe-based alloy powder
铁基自熔性合金粉末
5) Ni-based self-fluxing alloy powder
镍基自熔性合金粉末
1.
The Ni-based self-fluxing alloy powder coposite coating was produced on the substrate of ferrite and pearite base gray iron by the general electrical resistance furnace with graphite protection successfully.
用普通电阻炉加石墨保护的方法成功地在铁素体基灰铸铁及珠光体基灰铸铁基体上制备了镍基自熔性合金粉末复合材料。
6) self-fusing alloy powder Ni60
Ni60自熔性合金粉末
补充资料：自熔性球团矿
自熔性球团矿
fluxed pellet
2 1 rongx旧9 qiutuonkuang自熔性球团矿(fluxed pellet)碱度(Cao/5102)为。.8一1 .2的球团矿。单独用作高炉原料时，可以不加或少加熔剂。自熔性球团矿一般含铁62%左右，并含有CaO、MgO、5102、A12O3等，用同样的细铁精矿生产的自熔性球团矿与酸性球团矿相比较，前者含铁量较低、含硫较高。自熔性球团矿的气孔率较高，一般在25%左右，强度较低，但单个球的抗压强度也能达到Z000N以上，转鼓指数可达95%(150标准);真密度与原料的含铁量和球团矿的碱度有关，在4.5左右;视密度与气孔率关系密切在3.4左右。结晶良好的自熔性球团矿呈钢灰色，条痕为红褐色。 自熔性球团矿的矿物组成和结构比较复杂，但仍以赤铁矿(F eZO3)为主，赤铁矿连晶是其固结的基本形式。铁酸钙(C ao·FeZO3)为主要的私结相。少量的硅灰石(CaO·5102)和正硅酸钙(ZCaO·510。)分布在赤铁矿、铁酸钙颗粒之间的渣相中。由于自熔性球团矿液相较多，受表面张力的作用，气孔多呈圆形，且比酸性球团矿的气孔大，气孔率也较高，因而强度较低。但是仍能满足运输、贮存和高炉冶炼工艺的要求。它的还原性好，除了气孔率较高的原因外，它的主要矿物赤铁矿和铁酸钙都是易还原的矿物。特别是高温还原性明显地优于酸性球团矿。实验研究表明:自熔性球团矿在高温下(>1200℃)还原时，试样的表面与中心同时出现金属铁，铁酸钙被还原时析出的CaO与510:结合，形成正硅酸钙(ZCaO·5102)，从而避免了510:与FeO形成大量的液态渣相，并提高其还原性，试样中5102含量愈低，其高温还原性愈好。自熔性球团矿的还原膨胀率较高，但只要含碱金属不高，焙烧制度适宜，其还原膨胀率可以控制在允许的范围之内(不大于20%)。自熔性球团矿的焙烧温度区间较窄，对焙烧工艺制度要求严格，单位产品的燃料消耗较高。 (孔令坛)