1) blast cleaning
喷光处理
2) shot peening
喷丸处理
1.
Effects of shot peening on the selective oxidation of 1Cr13 alloy;
喷丸处理对1Cr13钢选择氧化的作用
2.
The analysis of SEM, EDS and the result of study show that although shot peening promotes the forming of protective Cr_2O_3 scale, it increases the compressive stress in the scales and the adhension property is poor; annealing eliminates the stress in the surface layer generated during peening and has function of low temperature pre-oxidation.
研究了经过喷丸处理及400℃退火处理的1Cr18Ni9Ti合金试样在900℃空气中的循环氧化性能。
3.
SEM, XRD and oxidation kinetics reults show that shot peening promotes the forming of protective Cr\-2O 3 scale, but the adhension property of the oxide scales is poor due to the increased compressive stress.
采用 4 0 0℃退火处理对喷丸处理的 1Cr18Ni9Ti合金进行了预处理 ,研究了不同处理的合金试样在 90 0℃空气中的恒温连续氧化性能。
3) Powder injection treatment
喷粉处理
4) Shot peening treatment
喷丸处理
1.
A nanostructured surface layer was fabricated on the hadfield steel by means of shot peening treatment.
采用表面喷丸处理的方法在高锰钢上制备出纳米结构表面,利用X射线衍射仪(XRD)、透射电镜(TEM)及高分辨透射电镜(HRTEM)研究由表面沿厚度方向的结构变化特征,并对显微硬度沿厚度方向的变化进行分析。
2.
The influence of shot peening treatment on the room temperature tensile properties of Ti-47.
0Cr(%,原子分数)的铸造TiAl合金进行喷丸处理实验,分析试样表面状态变化及其对室温拉伸性能的影响,结果表明,喷丸处理增加了表面粗糙度,改变了试样的表面形貌,使表面损伤痕迹的大小和方向均发生变化,且在试样的表面形成残余压应力,这些表面性质的改变程度均随喷射压强的提高而增大;喷丸试样的抗拉强度因表面压应力的存在而有所提高,但由于表面损伤和表面压应力的综合作用,其室温拉伸塑性在1×105Pa喷射压强下增加,而在2×105Pa和2。
3.
The resistance corrosion of zircaloy-4 by a shot peening treatment in autoclave steam at 673 K has been discussed with the oxide film component,topography,surface roughness,grain size and stress distribution according to XRD,SEM,AFM in this paper.
3MPa的高压釜中腐蚀,通过XRD、SEM、AFM分析喷丸处理后Zr-4合金形成的氧化膜与普通Zr-4合金形成的氧化膜的成分、形貌、表面粗糙度、晶粒尺寸大小及应力分布等。
5) shot-peening
喷丸处理
1.
The welding line surface of AISI304 stainless steel was processed by shot-peening treatment,the microstructures of the material surface were observed with optical microscope and scanning electron microscope.
对AISI304不锈钢氩弧焊缝表面进行了喷丸处理,通过光学显微镜和扫描电镜对材料表面及断口的微观组织进行了观察,用X射线应力衍射仪测试了喷丸处理前后试样的残余应力,并进行了在NaCl水溶液中的应力腐蚀试验。
2.
The effect of shot-peening on the surface roughness of NiCoCrAlY coating on Ni_3Al base alloy IC6 was investigated.
研究喷丸处理对IC6合金N iCoCrA lY涂层表面粗糙度的影响。
补充资料：喷光
分子式：
CAS号：
性质：喷光与喷上层以往有同一层意义，现在则出现一些区分。喷发层后可根据需要再加喷一道成膜或不成膜的光亮剂或光亮手感剂（一般不含着色剂），使革面更加光洁、滑爽，并改善革的防水性和防脱色性能。
CAS号：
性质：喷光与喷上层以往有同一层意义，现在则出现一些区分。喷发层后可根据需要再加喷一道成膜或不成膜的光亮剂或光亮手感剂（一般不含着色剂），使革面更加光洁、滑爽，并改善革的防水性和防脱色性能。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条