1) high i MnZn ferrite
锰锌系铁氧体材料高磁导率锰锌铁氧体μ
3) Mn-Zn ferrite iron core
锰锌系铁氧磁体铁芯
4) Mn-Zn soft magnetic ferrite
锰锌软磁铁氧体
1.
A novel technology,which is on the preparation of Mn-Zn soft magnetic ferrite using Fe,Mn and Zn existing in waste battery as raw materials,was proposed.
对废锌锰电池的综合利用的意义和方法进行了评述;提出了利用废锌锰电池中的Fe、Mn和Zn制备高档锰锌软磁铁氧体材料的新技术,并对其工艺流程、技术特点和经济指标进行了详细的阐述。
2.
Using pyrolusite,zinc concentration and iron scrap as materials,preparation of Mn-Zn soft magnetic ferrite was studied.
以软锰矿、硫化锌精矿及铁屑等为原料,研究了直接法制备锰锌软磁铁氧体的工艺条件,重点研究了浸出液复盐沉淀深度净化的工艺条件。
3.
In order to overcome the disadvantages of ceramics method and co-precipitation method on the preparation of Mn-Zn soft magnetic ferrite materials, we combined hydrometallurgy and inorganic chemical engineering with ferrite technology, and the direct-method on the preparation of Mn-Zn soft magnetic ferrite has been successfully developed.
针对“陶瓷法”和“共沉淀法”存在的问题，我们将无机化工、湿法冶金和磁性材料等学科进行交叉，成功开发出“直接法”制备锰锌软磁铁氧体材料新技术。
5) MnZn ferrite core
锰锌铁氧体磁芯
6) waste Mn-Zn ferrite powders
锰锌铁氧体废料
1.
On the basis of thermodynamics theory,and according to the content of Fe3+ in sulfuric acid leached liquor from waste Mn-Zn ferrite powders and the theoretical prescription of Mn-Zn ferrite,the sulfuric leached liquors’ proportion reduction processes,in which special proportion reducing agents of Fe,Mn and Zn powders were used,were studied.
在热力学理论分析的基础上,依据锰锌铁氧体废料硫酸浸液中Fe3+的量及铁氧体理论配方,研究利用金属铁粉、锰粉和锌粉对此浸出液的定比例还原过程。
补充资料：高锰酸锌
分子式： Zn(MnO4)2·6H2O
CAS号：
性质：黑色结晶，斜方晶系。密度2.45g/cm3。熔点90～105℃并开始分解。易溶于水。有潮解性。曝于空气或光中则分解。在醇中分解。宜于暗处密封贮藏。由高锰酸钡和硫酸锌反应制得。或由高锰酸钾与硫酸铝反应后溶液，再与锌盐反应制得。用作木材防腐剂，医药上用作收敛剂。
CAS号：
性质：黑色结晶，斜方晶系。密度2.45g/cm3。熔点90～105℃并开始分解。易溶于水。有潮解性。曝于空气或光中则分解。在醇中分解。宜于暗处密封贮藏。由高锰酸钡和硫酸锌反应制得。或由高锰酸钾与硫酸铝反应后溶液，再与锌盐反应制得。用作木材防腐剂，医药上用作收敛剂。