1) coarse-grained zone of HAZ
热影响区的粗晶区
2) coarse grained HAZ
热影响区粗晶区
1.
The effect of the local hard zone (LHZ) distributed in the coarse grained HAZ (CGHAZ) has been analyzed by 2-dimensional FEM on a mechanical model of the weld CGHAZ.
采用二维有限元数值方法分析了焊接热影响区粗晶区（ＣＧＨＡＺ）中局部硬化区（ＬＨＺ）的作用。
3) CGHAZ
粗晶热影响区
1.
Effect of Double Wire Welding Thermal Cycle on Microstructure and Properties of Ni-Cr Steel CGHAZ
双丝焊热循环对Ni-Cr钢粗晶热影响区组织性能的影响
2.
Research on Second Phase Particles in CGHAZ and Weld of Micro Alloyed Pipeline Steel
微合金管线钢焊接粗晶热影响区及焊缝的第二相粒子分析
3.
01V)and coarse grained heat affected zone(CGHAZ)of Ti-V-Nb microalloyed steel(0.
04Nb)模拟粗晶热影响区及焊缝(H08C焊丝%:0。
4) coarse grain heat affected zone
粗晶热影响区
1.
Microstructure of simulated coarse grain heat affected zone (CGHAZ) of Zr Microalloyed HSLA Steel are investigated using optical microscopy and transmission electron microscopy.
采用光学显微镜和透射电镜研究了锆处理对微合金钢粗晶热影响区组织的影响。
5) coarse-grained heat-affected zone(CGHAZ)
粗晶热影响区(CGHAZ)
6) coarse grain heat affect zone
粗晶热影响区
1.
The result shows that coarse grain heat affect zone (CGHAZ) becomes brittle.
利用热模拟技术进行了高强度船体用钢焊接热影响区组织、性能的模拟研究,结果表明,粗晶热影响区存在着脆化现象,随着焊接热输入的增加,粗晶热影响区奥氏体晶粒粗化,脆化加剧。
2.
The result shows that coarse grain heat affect zone (CGHAZ)becomes brittle.
利用热模拟技术还进行了 Q370q 桥梁用钢热影响区组织、性能的模拟研究,结果表明,粗晶热影响区存在着脆化现象,随着焊接热输入的增加,奥氏体晶粒粗化,脆化加剧。
补充资料：热影响区
热影响区
heat-affected zone
reylngx}QngqU热影响区(Heat一affeeted zone)焊接或切割过程中，母材因受热的影响(但未熔化)而发生金相组织和力学性能变化的区域。对于母材的焊接热影响区，由于在焊接热作用下重新经历了一次(单道焊)或多次(多道焊)的加热与冷却循环，必然伴有独具特征的一种物理冶金过程，或者说是一种特殊的热处理过程，从而不能不使原已是优质的母材性能发生某些变化，而且常常带来恶化效果(如硬化、软化或脆化)，甚至还可能发生各种类型的裂纹缺陷。因此，热影响区的性能变化是考察金属焊接性的重要一项。 (李维茜)