1) brittle type fracturing
脆型断裂
2) brittle crack of ratchet wheel form
棘轮型脆性断裂
3) hydrogen brittle fracture
氢脆断裂
1.
The result indicates that the tensile stress brought in spring by manufacture process and the hydrogen atoms filtered surface layer by pickling are main causes for delay fracture of spring,which is a kind of typical hydrogen brittle fracture.
对圆柱螺旋弹簧的断裂行为进行研究,结果表明:制造工艺引入到弹簧中的拉应力以及酸洗工艺渗入弹簧表层的氢原子是导致弹簧发生延迟断裂的主要原因,其断裂方式是一种典型的氢脆断裂。
4) brittle fracture
脆性断裂
1.
Numerical simulation of brittle fracture at V-shaped notches under mixed mode loading;
I-II复合型V型切口脆性断裂的数值模拟
2.
Maximum circumferential stress criterion of brittle fracture at the interface edge of bonded materials;
结合材料界面端脆性断裂的最大周向应力准则
5) brittle failure
脆性断裂
1.
The brittle failure of the foundation bolt for ladle turntable under the static load and low stress happens due to unsuitable between intensity and toughness in this high strength steel.
介绍了钢包回转台地脚螺栓在低应力状态下发生脆性断裂的实例。
2.
It has supplied advantageous scitific evidence to the anchor - chain's brittle failure at low temperature.
为锚链钢的低温脆性断裂提供了有利的科学依据。
3.
This paper analyses the reason that brittle failure is occurred and the factor that can influence brittle failure.
分析了钢结构发生脆性断裂的原因、影响结构脆性破坏的因素,提出了预防脆性破坏的措施。
6) Tough brittle fracture
韧脆断裂
补充资料：脆性断裂
分子式：
CAS号：
性质：不伴随有明显塑性形变的断裂现象。在应力-应变曲线上应力近乎线性地随应变而增长直至断裂。断裂对应的应变值一般小于5%。脆性断裂和韧性断裂的区别还表现在较低的断裂能和具有光滑特征的断裂面。同一聚合物材料在不同条件下可以表现为脆性断裂或韧性断裂。在较低的温度和较大的应变速度时容易发生脆性断裂。一般聚合物在明显低于玻璃化温度时往往表现出脆性断裂行为。随着温度升高，超过脆性-韧性转变温度时，断裂方式就变成韧性的。
CAS号：
性质：不伴随有明显塑性形变的断裂现象。在应力-应变曲线上应力近乎线性地随应变而增长直至断裂。断裂对应的应变值一般小于5%。脆性断裂和韧性断裂的区别还表现在较低的断裂能和具有光滑特征的断裂面。同一聚合物材料在不同条件下可以表现为脆性断裂或韧性断裂。在较低的温度和较大的应变速度时容易发生脆性断裂。一般聚合物在明显低于玻璃化温度时往往表现出脆性断裂行为。随着温度升高，超过脆性-韧性转变温度时，断裂方式就变成韧性的。