1) electro-slag welding
电渣焊接
2) electroslag welding joint
电渣焊接头
1.
The fracture mechanics experiments of Q235 electroslag welding joint with different technological procedure (anneal and normalize) were done in this paper.
本文对退火及正火(亚临界正火)两种工艺下的Q235钢板电渣焊接头进行断裂力学实验研究,分别对焊接接头的三个区域(焊缝、熔合区、热影响区)及母材的疲劳裂纹扩展速率、冲击韧性、断裂韧性进行测试。
3) pulsation welding
接触<电阻>电渣焊
4) electricity pressure weld
电渣压力焊接
1.
Design all adoptions HRB400 reinforcing bar(x-rated steel),under construction adoption roll-press thread connect,electricity pressure weld,flashlight weld,electricity weld takes to connect with colligation takes to connect various conjunctions method.
设计全部采用HRB400钢筋(三级钢),施工采用滚压直螺纹连接、电渣压力焊接、闪光对焊接、电弧焊搭接与绑扎搭接多种连接方法。
5) submerged slag pool welding
埋弧电渣焊接
6) welding slag
焊接熔渣
1.
Correlation between welding slag and usability quality of stainless steel electrode;
不锈钢焊条焊接熔渣及与焊条工艺质量的关系
补充资料：焊接:电渣焊
利用电流通过焊剂的熔渣所產生的电阻热熔化工件材料(母材)和填充金属的焊接方法。熔渣还对熔池起保护和净化的作用。电渣焊一般是垂直向上施焊。填充金属有单焊丝﹑多焊丝﹑焊丝加熔嘴(见图 电渣焊示意图
)和金属板等形式。焊丝连续送进。电渣焊适於焊接20毫米以上厚大截面的工件。它主要用於焊接厚壁压力容器﹑大型铸-焊结构﹑锻-焊结构或厚板拼焊﹐还可用於堆焊轧辊﹑高炉料鐘等大型工件。电渣焊可焊接低碳钢﹑低合金钢﹑中碳钢﹑某些不锈钢和纯铝等。电渣焊生產效率高﹐焊缝金属缺陷少﹐劳动卫生条件好﹐是重型机械製造中重要的焊接方法之一。它的缺点是输入的热量大﹐接头在高温下停留时间长﹑焊缝附近容易过热﹐焊缝金属呈粗大结晶的铸态组织﹐衝击韧性低﹐焊件在焊后一般需要进行正火和回火热处理。(见彩图 电渣焊
)
)和金属板等形式。焊丝连续送进。电渣焊适於焊接20毫米以上厚大截面的工件。它主要用於焊接厚壁压力容器﹑大型铸-焊结构﹑锻-焊结构或厚板拼焊﹐还可用於堆焊轧辊﹑高炉料鐘等大型工件。电渣焊可焊接低碳钢﹑低合金钢﹑中碳钢﹑某些不锈钢和纯铝等。电渣焊生產效率高﹐焊缝金属缺陷少﹐劳动卫生条件好﹐是重型机械製造中重要的焊接方法之一。它的缺点是输入的热量大﹐接头在高温下停留时间长﹑焊缝附近容易过热﹐焊缝金属呈粗大结晶的铸态组织﹐衝击韧性低﹐焊件在焊后一般需要进行正火和回火热处理。(见彩图 电渣焊 )