1) gas shielded magnetic flux arc welding
磁性气体保护焊
2) gas shielded magnetic flux arc weling
磁性焊剂气体保护焊
4) gas shielded arc welding
气体保护焊
1.
To reveal the influence of forced convection on gas shielded arc welding temperature field,the infrared camera was used to investigate the temperature field of the base metal in CO2 arc welding.
为了研究强制对流对气体保护焊温度场的影响,通过红外热像仪检测了CO2气体保护焊的温度场,发现在熔池及其邻近区域温度呈圆锥型分布。
2.
According to the welding technological requirement of West-to-East Gas Transportation Project,an experimental research was performed in this paper on gas shielded arc welding of 10.
3mm X70管线钢进行了气体保护焊试验。
5) gas metal arc welding
气体保护焊
1.
Development of gas metal arc welding wire for X80 pipeline steel;
X80管线钢气体保护焊用焊丝的研制
2.
Modeling and analysis of droplet forming in gas metal arc welding short circuiting transfer;
气体保护焊短路过渡熔滴成形的建模分析
3.
A novel digital waveform control scheme for CO_2 gas metal arc welding
CO_2气体保护焊的新型全数字化波形控制技术
6) gas shielded welding
气体保护焊
1.
Several new type of methods for wire feeding in gas shielded welding;
气体保护焊中几种新型送丝方法
2.
The gas shielded welding is applied to the longitudinal welding seam on the air reservior of freight cars, various factors effecting welding quality have been analyzed through multi times adjustments and tests, the results indicate that the reasonable & compatible welding parameters and scientific swing welding methods can ensure the good internal and external welding quality of welds.
采用气体保护焊对货车用储风缸的纵缝进行焊接 ,通过反复调试 ,研究了影响焊接质量的各种因素。
3.
Implant tests were conducted on l5MnVN steel using Ar+20%CO_2 gas shielded welding process,The test results have shown that when the welding heat inp(?)t is in the range of l5～40kJ/cm the critical stresses of the implant specimen are all above the yielding strength of l5MnVN steel and are higher than that of the specimen welded with J507 and J557MoV welding electrodes.
用Ar+20%CO_2气体保护焊方法对15MnVN钢进行插销试验,试验结果表明,焊接线能量在15～40kJ/cm范围内,插销试样的临界应力高于15MnVN钢的屈服极限,高于用J507焊条及J557MoV焊条手工焊的插销临界应力。
补充资料：二氧化碳气体保护焊
二氧化碳气体保护焊
CO_(2) welding
eryanghuatanq(tlboohu han二氧化碳气体保护焊(CO。welding)二氧化碳气体保护焊是以二氧化碳作为保护介质、以连续送进的焊丝为电极的熔化极气体保护电弧焊焊接方法。二氧化碳焊接设备包括电源、焊枪、CO:气体源和焊丝驱动机构。 二氧化碳气体保护焊具有成本低、抗氢气孔能力强、适合薄板焊接、易进行全位置焊等优点，广泛应用于低碳钢和低合金钢等黑色金属材料的焊接。它的主要缺点是焊接过程中产生金属飞溅。 二氧化碳气体保护焊的焊丝设计、制造和使用原则除与MIG焊有相同之处外，还对焊丝的化学成分有特殊要求:焊丝必须有足够数量的脱氧元素;焊丝的含碳量要低，一般要求C<。·11%，这是由于C02气体具有氧化性的缘故。 (田志凌)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。