1) overannnealing
过度退火
2) overannealing
[,əuvərə'ni:liŋ]
过退火
3) annealing temperature
退火温度
1.
Effect of annealing temperature on the microstructure of rapidly-solidified TiNi-Cu alloy ribbons;
退火温度对Ti_(53.5)Ni_(22.8)Cu_(23.7)合金快速凝固条带组织的影响
2.
Influence of annealing temperature on structure and properties of Al-6Mg-Sc-Zr alloy;
退火温度对Al-6Mg-Sc-Zr合金组织与性能的影响
3.
Effects of annealing temperature on microstructures and properties of the 25Mn-3Si-3Al-TWIP steel;
退火温度对25Mn-3Si-3Al-TWIP钢组织和力学性能的影响
4) anneal temperature
退火温度
1.
Effect of anneal temperature on performance of poly(chloro-p-xylylene)films;
退火温度对聚氯代对二甲苯膜性能的影响
2.
Taking original shape examination as contrast,the HT250 welding strain under three kinds of different anneal temperature(500℃、600℃、650℃)was studied.
以未进行退火处理试件为对比,研究了三种不同的退火温度(500℃、600℃、650℃)对HT250焊接残余应力的影响;对四块试件分别测试了各自的焊接应力,并将测试数据输入计算机得到了不同退火温度下的试件的焊接应力曲线;结果表明:此试验的最佳退火温度为650℃。
3.
The paper studies the effect of different cold deformation and anneal temperature as well as holding time on the material organization and property of alloy pipe 5086,sets the production process system of aluminum alloy 5086 at state of H34.
研究了不同冷变形程度、退火温度与保温时间对5086铝合金管材组织及性能的影响,确定5086铝合金H34状态的生产工艺制度,在工业生产条件下,其产品的技术指标达到了用户要求。
5) annealed hardness
退火硬度
1.
Thus the metallographic structure whichaccords with standard annealed hardness is obtained.
本文通过对冷作模具钢X45NiCrMo4锻制扁钢退火工艺的研究和改进，获得了符合标准退火硬度值的金相组织，并运用于大生产实践，取得了满意的效果。
补充资料：软化退火(见低温退火)
软化退火(见低温退火)
soft-annealing
rU0nhUO tUihUO软化退火(soft一annealing)见低温退火。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。