1) Galvanized Steel Corrugated Sheet
镀锌波纹钢板
2) galvanized sheet steel
镀锌钢板
1.
The commercial hot-dip galvanized sheet steel was investigated for its corrosion behavior in three different seawater zones in Qingdao with electrochemical measurement,weight loss test and SEM.
开展了热镀锌钢板在青岛不同海水区带的实海腐蚀测试,并利用电化学测试、失重腐蚀测试和扫描电镜研究了镀层的海水腐蚀行为。
2.
With the rapid development of Chinese economy, demands for galvanized sheet steels increased significantly because of the rapid development of construction and automotive industry during the last decade.
随着国内经济的持续稳定发展,在过去的10年中,由于建筑和汽车行业的快速发展,对镀锌钢板的需求持续旺盛。
3.
occured in forming and after coating of the prephosphating galvanized sheet steel,this paper demonstrates analyses on all kinds of influential factors happened in production and forming in detail,after that,provides some solutions on purpose.
为解决预磷化镀锌钢板加工成形、涂装后易出现的条影、针孔、粗糙等问题,对其生产及加工成形过程中的各种影响因素进行了详细分析,并有针对性地提出一般的解决办法。
3) zinc coated steel
镀锌钢板
1.
Effect of TiC coating on electrode tip surface on electrode degradation during resistance spot welding zinc coated steel;
点焊镀锌钢板时电极表面熔敷TiC涂层对电极失效的影响
2.
Effect of zinc coating on arc heating behavior for joining Al and zinc coated steel by welding-brazing process
镀锌层对铝/镀锌钢板CMT熔-钎焊电弧加热行为的影响
3.
The effect of TiC coating in electrode tip surface on spheriform electrode degradation during resistance spot welding zinc coated steel was investigated by SEM,EDX and XRD.
利用SEM、EDX和XRD等方法分析了在点焊镀锌钢板时球形电极表面熔敷TiC涂层对电极失效的影响。
4) galvanized steel
镀锌钢板
1.
Study on the effects of components in phosphating solution on properties of phosphating film of galvanized steel;
镀锌钢板磷化液组分对磷化膜性能的影响
2.
The film forming mechanism of a novel calcium modified phosphating solution on galvanized steel was studied.
研究了一种新型的钙改性磷化液在镀锌钢板上的成膜机理。
3.
A Phosphating process for galvanized steel plate was developed.
研究出一种应用于镀锌钢板的磷化工艺,对磷化液中各组分的作用进行了分析、讨论,尤其氯离子对磷化膜性能的影响。
5) zinc coated steels
镀锌钢板
1.
5wt% has been studied during spot welding of zinc coated steels .
5 %的铜基复合材料 (Ti B2 /Cu)作电极在点焊镀锌钢板时的失效形式 ,结果表明 :Ti B2 /Cu电极在点焊镀锌钢板时的平均使用寿命是 Cu Cr Zr合金电极的 4倍 ,Ti B2 /Cu电极的失效形式主要是表面的合金化 ,少量的细碎翻边、粘附和坑蚀 ,不出现蘑菇状 ,是一种较好的点焊电极材
2.
A series of spot welding technology and joint tensile shear tests for uncoated low carbon, electroplated and two kinds of hot dipped zinc coated steels were made to improve the quality of spot welding joint for zinc coated steels.
为提高镀锌钢板点焊接头的质量，对普通冷轧钢板、电镀锌钢板和两种镀锌层厚度不同的热镀锌钢板进行了一组点焊工艺及接点强度试验，并对试验结果进行了计算机回归分析，分别得出了这几种材料在不同的焊接电流、焊接时间下的点焊熔核直径或接头拉剪强度变化曲线以及点焊飞溅临界曲线。
6) galvanized steel sheet
镀锌钢板
1.
Nucleation mechanism of spot welding galvanized steel sheet;
镀锌钢板点焊形核机理的研究
2.
Forecast of electrode life in spot welding of galvanized steel sheet;
镀锌钢板点焊电极寿命预测
3.
CO_2 laser-weldability of galvanized steel sheets;
镀锌钢板的CO_2激光焊焊接性
补充资料：镀锌钢板
镀锌钢板
galvanized sheet steel
dux一n gongban镀锌钢板(galvanized sheet steel)表面镀有锌(或锌合金)层的。.3一3.omm厚的薄钢板，是-种主要的表面防护冶金产品。它具有优良的耐大气腐蚀性能。锌层在大气环境中其表面能形成防蚀保护膜，保护内部的钢基体，而且锌作为阳极性的镀层又可对钢基体有阴极保护作用，综合地延长钢板的使用寿命，此外镀锌层也具有美观装饰作用。镀锌钢板广泛用于建筑、车辆、电气设备、家用电器和各种日常用品等。 镀锌钢板有热浸镀法和电镀法两种生产工艺，产品品种各不相同。 热镀锌钢板最早于19世纪初在欧洲开始用熔剂法制造。在20世纪随着带钢冷轧生产工艺的进展，1927年波兰人森吉米尔(T.Sendzimir)将带钢退火和热镀锌工艺结合而发明了分解氨保护气体还原法进行带钢连续热镀锌，提高了产品质量和生产效率。此后热镀锌钢板生产在该工艺基础上迅速发展。 热镀锌钢板的品种规格国际上的规定大致相同。按镀锌量，在120~6109/m“(以两面镀锌量之和表示)的范围内分成6个等级供货。按力学性能分级，有普通级、冲压加工级、深冲级和高强度级等品种。按表面锌‘花形状有普通锌花、小锌花和无锌花等。按镀后处理有铬酸盐钝化处理、磷酸盐处理、涂油处理等，或在镀后经平整机或光整机加工处理。还有一种称为合金化热镀锌钢板的品种(美国商标名为Galvaneal)，为带钢在热浸镀后经过在线的合金化加热炉处理，使镀锌层转变成含铁约10%的锌一铁合金层，有更好的耐蚀性和涂装性，适合某些用户的专门需求。有的生产线还有单面热镀锌钢板的品种，由于生产工艺复杂，并不普遍。为进一步提高热镀锌钢板的耐蚀性，已研制开发多种锌一铝合金热镀钢板，较成熟的有两种，可在稍加改造的热镀生产线上生产。一种是美国伯利恒钢铁公苛1972年开发的铝一锌合金镀层钢板，镀层成分是55%AI一43.5%Zn一1.5%51，美国商标名Galvalume，其盐雾试验耐蚀寿命是热镀锌钢板的2一4倍。另一种是设在美国的国际铅锌研究组织(ILZRO，International Leadzinc Researeh organization)于1951年开发的锌一铝合金镀层钢板，镀层成分为含有0.1%饰斓混合稀土的锌一5肠铝合金，国际商标名为Galfan，其盐雾试验耐蚀寿命是热镀锌钢板的2~3倍，其独特之点是镀层和钢板基体之间没有脆性合金层，所以具有更好的成形性和涂装性。这两种产品的生产和应用正在逐步推广。 电镀锌钢板用带钢连续电镀法生产，最早始于2。