1) Abnormal Structure Steel
反常组织钢
2) abnormal structure steel
反常组织(的)钢
3) abnormal steel
反常钢
4) abnormal structure
异常组织
1.
Through the analysis for feed material bought and drawn of several kinds of possible flaws such as impunity,decarbonization,surface defect,abnormal structure that result in the premature invalidation of spring in serve were put forward in this paper.
提出了几种可能导致弹簧在使用过程中发生过早失效的缺陷,例如:夹杂、脱碳、表面缺陷、异常组织等,并对这些缺陷的形成原因和对弹簧失效的影响作了分析。
2.
By analyzing the result of the experiment, it reveals that the abnormal structure usually appears at the surface layer of nodular iron castings produced by furan-sulfonic acid, toluene sulfonic acid (TSA), cured sand mold with the nodulizing agent, Mg-RE alloy.
通过实验研究,用甲苯磺酸作催化剂的呋喃树脂自硬砂与稀土镁作催化剂生产的球铁件,通常在其铸件表层出现异常组织。
3.
The abnormal structure usually appears at the surface layer of nodular iron castings produced by furan-sulfonic acid cured sand mold.
本实验研究查明,当用甲苯磺酸作催化剂的呋喃树脂自硬砂生产稀土镁球铁件时,通常在其铸件表层出现异常组织。
5) structure abnormity
组织异常
1.
Wire shall be caused composition segregation,structure abnormity and serious crack in the process of cold heading.
中碳冷镦钢是中、高强度紧固件的主要原材料,连铸过程中铸坯表面增碳,将会造成线材成分偏析、组织异常,镦打过程中严重开裂。
6) normal tissue
正常组织
1.
Methods The expression of PBK/TOPK was detected in normal tissues including 19 types of normal human tissue and tumor tissues including 19 types of tumors by using tissue microarray and EnVision immunohistochemical staining.
目的观察PBK/TOPK在人体正常组织和常见恶性肿瘤组织的分布和表达,探讨作为肿瘤标志物的可能性。
2.
In this article,a cooling method was proposed for protecting the normal tissue or organ surrounding the tumor during hyperthermia treatment.
本文提出了一种对热疗中肿瘤周围的正常组织或器官实施降温保护的方法。
补充资料：反常组织
abnormalstructure：渗过碳的钢内有时出现这样的组织，即大块渗碳体和其四周被游离铁素体所包围着的组织。这样的组织，在正常的情况下是不出现的，故称“反常组织”。