1) pitting
[英]['pitiŋ] [美]['pɪtɪŋ]
孔蚀;点蚀
2) spot corrosion hole
点蚀孔洞
3) pitting corrosion
孔蚀;麻点腐蚀
4) pitting
[英]['pitiŋ] [美]['pɪtɪŋ]
孔蚀
1.
Effects of Nickel Content and Simulated Heat Affected Zone of 2205 Duplex Stainless Steel on Pitting Corrosion;
合金元素及模拟热处理对2205双相不锈钢之孔蚀性质影响
2.
The influence of different concentrations of CO2-3 on the resistance to pitting corrosion was investigated in bittern for 2205DSS by electrochemical polarization carves and electrochemical impedance spectra.
利用电化学交流阻抗技术研究CO32-浓度变化对2205DSS在盐卤中耐孔蚀行为的影响;采用失重试验法进行加速腐蚀试验,并与电化学实验结果进行对比;使用原子力显微镜表征2205DSS的腐蚀形貌图,计算小孔的平均深度,分析表面粗糙度。
3.
The electrochemical characteristics of pitting corrosion of X70 pipeline steel in phosphate buffer solution were studied in this paper.
研究了X70钢在磷酸盐缓冲溶液中的亚稳态与稳态孔蚀的电化学行为特征。
5) pitting corrosion
孔蚀
1.
On the inhibiting law and its mechanism of rare earth for the pitting corrosion of aluminium alldy in aqueous chloride solution;
稀土在含C1ˉ介质中对铝合金孔蚀的缓蚀规律及机理研究
2.
Features of electrochemical noise during pitting corrosion of 2024-T3 aluminum alloy in 3.0% Na_2SO_4 solution;
硫酸钠溶液中2024-T3铝合金孔蚀过程的电化学噪声特征
6) pit corrosion
孔蚀
1.
The results demonstrate that corrosion inhibitors of organic phosphonale/zinc salts and complexing agent exhibit corrosion inhibition of 20 # carbon steel in high-concentration chlorine ion solution, but they can not control the pit corrosion of stainless steels.
结果表明:有机膦酸盐/锌盐类缓蚀剂及其复合剂对高浓度氯离子溶液中的20号碳钢的腐蚀有抑制作用,但不能抑制不锈钢的孔蚀;钼酸钠加速不锈钢的孔蚀,十二烷基硫酸钠、十二烷基磺酸钠和十二烷基苯磺酸钠等含有较长碳链的表面活性剂可提高不锈钢孔蚀的击穿电位,且与十二醇复配后具有协同缓蚀作用,对抑制孔蚀的发生有效。
2.
The results show that the stainless steels suffered fast general corrosion and pit corrosion in the two mediums.
结果表明 ,两种不锈钢在两种介质中都遭受较为严重的均匀腐蚀和不同程度的孔蚀 ,腐蚀程度和系统内温度有关 ,最严重的腐蚀发生在临界温度附
3.
This paper expounds corrosion mechanism of chlorine io n on stainless steel by absorption theory and film forming theory, introduces co rrosion mechanism of stress and pit corrosion on compression tank of stainless s teel, and puts forward appropriate preventive measures.
用吸附理论及成相膜理论解释了氯离子对不锈钢的腐蚀原理 ,介绍了应力腐蚀、孔蚀使不锈钢制压力容器腐蚀失效的机理 ,并提出了相应的预防措
补充资料：孔蚀
分子式：
CAS号：
性质：又称坑蚀，斑点腐蚀，小孔腐蚀或点蚀。金属表面大部分区域腐蚀相对较轻，而某些局部出现向纵深发展的腐蚀小孔的腐蚀形态。孔蚀的原因是活性阴离子导致表面钝化膜局部破坏。具有钝化能力的金属如不锈钢、铝合金及碳钢等，在含氯离子介质中经常发生孔蚀。蚀孔的发展速度有时很快，可以深入金属甚至短时间内蚀穿金属截面，且较难预测，因此孔蚀往往比均匀腐蚀具有更大的危害性。可以通过降低介质中的有害阴离子浓度，采用涂层保护、添加缓蚀剂和阴极保护等方法予以减轻或防止。
CAS号：
性质：又称坑蚀，斑点腐蚀，小孔腐蚀或点蚀。金属表面大部分区域腐蚀相对较轻，而某些局部出现向纵深发展的腐蚀小孔的腐蚀形态。孔蚀的原因是活性阴离子导致表面钝化膜局部破坏。具有钝化能力的金属如不锈钢、铝合金及碳钢等，在含氯离子介质中经常发生孔蚀。蚀孔的发展速度有时很快，可以深入金属甚至短时间内蚀穿金属截面，且较难预测，因此孔蚀往往比均匀腐蚀具有更大的危害性。可以通过降低介质中的有害阴离子浓度，采用涂层保护、添加缓蚀剂和阴极保护等方法予以减轻或防止。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条