1) accelerated aging test
加速老化试验，人工老化试验
2) artificial accelerated ageing test
人工加速老化试验
1.
This paper contrastively analyzes the field exposure test and artificial accelerated ageing test data in the South China Sea about the fluorocarbon coatings for the anticorrosion engineering of Main Gymnasium of Olympic Games and other fluorocarbon coatings, giving the, differences among every type of fluorocarbon resin coatings about their aging-resistance.
介绍了奥运主体育场"鸟巢"防腐工程用氟碳涂料与其它类型氟碳树脂涂料在海南的天然曝晒试验数据与人工加速老化试验数据对比分析,并详细阐述了各种类型氟碳树脂涂料在耐老化性方面存在差异的原因。
2.
The photo-oxidation ageing process of polypropylene filaments was studied by artificial accelerated ageing test using different intensities of UV irradiation.
以聚丙烯长丝为对象,采用不同紫外线辐射强度的人工加速老化试验对其光氧老化过程进行研究。
3) artificial weathering test
人工气候加速老化试验
4) accelerated aging test
加速老化试验
1.
This article studies the impact of the accelerated aging test to UF MDF decorated by different material about physical and mechanical properties.
研究了加速老化试验对经不同装饰后的脲醛胶中纤板物理力学性能的影响。
2.
A accelerated aging test of ethylene propylene rubber M204 and M209 7 in propellant was carried out.
进行了乙丙胶M 2 0 4和M 2 0 9 7在推进剂中的加速老化试验 ,经过对试验数据的处理 ,初步发现时间外延方法适用于预测橡胶材料在特种介质中的老化性能变
3.
In this paper, the accelerated aging tests at several higher temperatures are carried out for a kind of RDX compound explosive charge used in a certain missile warhead.
通过高温加速老化试验和统计分析,研究了某导弹战斗部中炸药装药的贮存寿命分布规律,在此基础上,建立了贮存寿命的可靠性评估模型,并对贮存温度下的平均贮存寿命及贮存寿命置信下限进行了评估。
5) accelerated ageing test
加速老化试验
1.
The oxidation stability of lubricating oils including 30# machinery oil, 4106# and 4109# aircraft lubricating oils was studied out by accelerated ageing test According to the property-aging time relation and Arrhenius formulation, the ageing dynamic equation of variance ratios of viscosity of 30# machinery oil was obtained by linear regression method.
对30#机械油与4106#和4109#航空润滑油进行了加速老化试验;在此基础上,运用阿累尼乌斯方程和性能变化的时温关系式,采用线性回归方法推导出30#机械油粘度变化的老化动力学方程,以粘度增加率20％为使用极限值,预测它在25℃条件下的贮存年限为12 a。
6) accelerated aging experiment
加速老化试验
1.
It is designed accelerated aging experiments with different salt steam temperature and aging time.
本文在总结复合材料在海洋的盐雾环境中使用的材料腐蚀理论基础上,分析复合材料发生腐蚀的主要形式和历程,模拟自然环境试验设计不同盐雾温度、不同老化时间下的加速老化试验,通过材料表面形貌、玻璃化转变温度、微观结构的变化来评价玻璃钢在盐雾中的腐蚀性能,着重分析温度、时间对材料腐蚀性能的影响规律;根据中值老化寿命和剩余强度之间的关系式,建立了加速寿命规律模型和寿命预测模型;根据试验中玻璃钢力学性能随老化时间的衰减多数情况下具有一致的规律性,建立了盐雾环境中玻璃钢力学性能随老化时间的衰减三线型模型。
补充资料：加速老化试验
分子式：
CAS号：
性质：为评价橡胶耐老化性能，将橡胶置于受控的苛刻条件下，以在较短时间产生与自然老化相似效果而进行老化的过程。通常加速老化条件为：在提高温度下让橡胶在空气、氧、臭氧或其他腐蚀性介质中进行试验，以寻找出在试验条件和产品实际使用条件下，橡胶耐老化性能之间的相关性。
CAS号：
性质：为评价橡胶耐老化性能，将橡胶置于受控的苛刻条件下，以在较短时间产生与自然老化相似效果而进行老化的过程。通常加速老化条件为：在提高温度下让橡胶在空气、氧、臭氧或其他腐蚀性介质中进行试验，以寻找出在试验条件和产品实际使用条件下，橡胶耐老化性能之间的相关性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条