1) p-styrenesulfonic acid
p-苯乙烯磺酸
2) Butyl p-styrenesulfonate
P-乙烯基苯磺酸正丁酯
3) isobutyl p-styrenesulfonate
p乙烯基苯磺酸异丁酯
1.
To design high affinity switchable imaging system,a monomer isobutyl p-styrenesulfonate(IBSS) and its copolymer with styrene(St) and methacrylic acid(MAA) were synthesized.
为了构筑高亲和性变化成像体系,合成了p乙烯基苯磺酸异丁酯单体(IBSS),并将其与苯乙烯(St),甲基丙烯酸(MAA)共聚得到一种热敏树脂,通过IR1、H NMR、GPC、DSC、TG分别确认了其结构、组成、分子量、热分解和热稳定性,并采用该树脂与红外染料匹配构筑热敏成像体系。
4) styrene sulfonic acid
苯乙烯磺酸
1.
IA-SSA copolymer,a scale inhibitor,was synthesized from itaconic acid (IA) and styrene sulfonic acid (SSA).
以衣康酸 (IA)和苯乙烯磺酸 (SSA)为原料 ,合成IA/SSA共聚物阻垢剂 ,确定的最佳合成条件 :反应温度为 10 3℃ ,反应时间为 2h ,引发剂用量为 7% (占单体总质量 ) ,IA∶SSA质量比为 2 8∶1。
5) N,N-bis(Polyoxyethylene)-p-toluenesulfonic acid amide
N,N-二(聚氧乙烯)-P-甲苯磺酸酰胺
6) polystyrene sulfonic acid
聚苯乙烯磺酸
1.
In the aqueous phase,choosing polystyrene sulfonic acid as template doping agent,polyvinyl alcohol as film-forming agent,and aniline as monomer,and utilizing ammonium persulfate to initiate and synthesize the complex solid of PANI/PSSA-PVA,and it's aqueous solution,and then with the method of spin-coating,the corresponding complex electrochromic films is prepared.
在水相中,以聚苯乙烯磺酸(PSSA)为模板掺杂剂,聚乙烯醇(PVA)为成膜助剂,苯胺(An)为单体,过硫酸铵(APS)引发合成水溶性导电聚苯胺/聚苯乙烯磺酸-聚乙烯醇(PANI/PSSA-PVA)复合物固体及其复合溶液,用旋涂法制备了相应的复合电致变色膜。
2.
Water soluble conductive polyaniline (PAn) was synthesized by the oxidation of aniline(An) doped with ammonium persulfate(APS) and polystyrene sulfonic acid(PSSA) through the method of emulsion polymerization.
以苯胺(An)为单体,过硫酸铵(APS)为引发剂,采用现场乳液聚合法合成了可完全溶于水的聚苯乙烯磺酸(PSSA)掺杂聚苯胺(PAn)。
补充资料：石油磺酸苯酯
分子式：
分子量：
CAS号：
性质：浅黄色油状物。密度1.03-1.06。酸值小于0.1。闪点200-220℃。电性能和机械性能良好，挥发性小，无毒，但互溶性和耐寒性较差。用作聚氯乙烯的主增塑剂。由C12-C18的液态石蜡经氯磺酰化后，再和苯酚酯化而制得。
分子量：
CAS号：
性质：浅黄色油状物。密度1.03-1.06。酸值小于0.1。闪点200-220℃。电性能和机械性能良好，挥发性小，无毒，但互溶性和耐寒性较差。用作聚氯乙烯的主增塑剂。由C12-C18的液态石蜡经氯磺酰化后，再和苯酚酯化而制得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。