1) High-angle boundary
高角晶界
2) misorientation angle
晶界角
1.
The influence of the substrate thickness on cube texture,misorientation angle and average grain size was studied.
主要研究基带厚度对其立方织构、晶界角分布以及晶粒尺寸的影响。
3) low-angle boundary
小角晶界
1.
Two kinds of low-angle boundary (mosaic structure) in Ce:YAP were observed by etching figures and rocking-curve.
通过腐蚀形貌和XRD摇摆曲线,观察到了垂直和平行于Ce:YAP[010]方向的两组晶面内存在的小角度晶界(镶嵌结构间界),根据SEM形貌估算出(010)面内小角晶界的夹角为51”;四晶XRD摇摆曲线的结果表明,平行于[010]向的晶面内小角晶界的夹角为58”;摇摆曲线的半峰宽为54”,根据Darwin理论算出理想晶体的半峰宽为17”,并由此分析了晶体的完整性。
4) large boundary
大角晶界
1.
e acicular ferrite and quasi-polygonal ferrite,which the grain boundaries between them are large boundary.
通过 OM、SEM、TEM、EBSD 等手段研究了针状铁索体+准多边形铁素体的复合组织的 F40级船板钢的低温冲击韧性及其机理,由于这种复合组织之间界面均为大角晶界,晶界上存在大量被细小析出所钉扎的位错,对裂纹的扩展起到有效的阻碍作用,使得组织具有良好的低温韧性,-80℃的冲击功可以达到138J 以上。
5) high angle grain boundary
大角度晶界
1.
Since the dislocations started,moved and effected at each other during the deformation process,the portion of high angle grain boundary achieved a peak value in grain boundary distribution at a strain of 1%.
由于形变过程中位错开动、运动及相互作用等因素,大角度晶界在总晶界中的比例在应变1%处达到一个峰值。
6) low angle boundary
小角度晶界
1.
The transverse tensile properties and fracture behaviour of the twist low angle boundary of DD6 single crystal superalloy were investigated at 760℃,850℃ and 980℃.
在760℃,850℃和980℃温度条件下,研究了DD6单晶高温合金扭转小角度晶界的横向拉伸性能和断裂特征。
补充资料：晶界
分子式：
分子量：
CAS号：
性质：晶界是结构相同而取向不同晶体之间的界面。在晶界面上，原子排列从一个取向过渡到另一个取向，故晶界处原子排列处于过渡状态。
分子量：
CAS号：
性质：晶界是结构相同而取向不同晶体之间的界面。在晶界面上，原子排列从一个取向过渡到另一个取向，故晶界处原子排列处于过渡状态。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条