1) Fusion range
熔融区
2) Zone Melting
区域熔融
1.
In order to improving the purity of the industrial product,antioxidant D was purified by the methods of Recrystalize and Zone Melting.
用重结晶和区域熔融法提纯制备标准物质用N-苯基-β萘胺(防老剂D)。
2.
In order to improve the purity of industrial product,Antioxidant BHT was purified by the methods of recrystalize and zone melting.
为提高防老剂BHT的纯度,采用重结晶和区域熔融法对工业品防老剂BHT进行提纯。
3.
In order to meet the demand of high-pure phosphoric acid and semiconductor industries, a combined theoretical and experimental approach was undertaken to find out the influences of zone length and times of zone pass on the solute distribution in ingot after the purification process of industrial yellow phosphorus by zone melting method.
为了满足高纯磷酸以及半导体等行业对高纯磷的需求,采用了区域熔融法对工业黄磷进行提纯,分析了区熔法提纯工业黄磷的原理,并根据所测有效分布系数建立整个区熔过程中杂质分布的数学模型。
3) Sub-melting zone
熔融子区
4) zone melting
区域融熔
5) zone melting
区域熔融[炼]
补充资料：区域熔融
简称区熔法。根据液固平衡原理，利用熔融－固化过程以去除杂质的方法。区域熔融可把杂质从一个元素或化合物中除掉，以达到提纯的目的。也可把需要的杂质重新均匀分配于一个物质中，以控制它的成分。区域熔融在纯化金属上是最有用的方法。应用这种技术一般可使纯度达到99.999％。
区域熔融过程是将样品做成薄杆状，长度为0.6～3米或更长。这个杆状物封闭在一个管内，水平或垂直地悬浮着。一个能够加热的窄环套在它的周围。环的温度保持在这个固体的熔点以上几度。窄环以极慢速度(1～3米／时)沿着杆状物移动。在样品中，实际上等于一个窄的熔融区沿着杆状物前进。区域的前边形成液体，而固体则在后面沉淀出来。较易熔于液相而难熔于固相的杂质，跟随这个熔融区。较难熔于液相的，就留在后面。杂质的存在，能降低一种物质的凝固点。熔融区向前移动时，更多的杂质就浓集在它后面凝固的部分。操作终了时，把杆状物后端凝固的杂质，简单地切去即可。经过多次重复操作，可以达到高度纯化。环的操作可以循环多次，也可以同时使用几个环，这个过程叫做区域精制。熔融区沿着杆状物前后移动，则可降低成分的区别，使这个物质恢复均匀性，这个过程叫做区域调平。
应用区域熔融法精制金属、半导体、化合物，以及感光药品，如卤化银等，可以得到高度纯化的产品。使用此法可使半导体物质中的有害不纯物降低到 1×10-10。
区域熔融过程是将样品做成薄杆状，长度为0.6～3米或更长。这个杆状物封闭在一个管内，水平或垂直地悬浮着。一个能够加热的窄环套在它的周围。环的温度保持在这个固体的熔点以上几度。窄环以极慢速度(1～3米／时)沿着杆状物移动。在样品中，实际上等于一个窄的熔融区沿着杆状物前进。区域的前边形成液体，而固体则在后面沉淀出来。较易熔于液相而难熔于固相的杂质，跟随这个熔融区。较难熔于液相的，就留在后面。杂质的存在，能降低一种物质的凝固点。熔融区向前移动时，更多的杂质就浓集在它后面凝固的部分。操作终了时，把杆状物后端凝固的杂质，简单地切去即可。经过多次重复操作，可以达到高度纯化。环的操作可以循环多次，也可以同时使用几个环，这个过程叫做区域精制。熔融区沿着杆状物前后移动，则可降低成分的区别，使这个物质恢复均匀性，这个过程叫做区域调平。
应用区域熔融法精制金属、半导体、化合物，以及感光药品，如卤化银等，可以得到高度纯化的产品。使用此法可使半导体物质中的有害不纯物降低到 1×10-10。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。