1) dry copper
乾铜(含多量氧化亚铜之脆性铜)
2) copper-cuprous oxide
铜-氧化亚铜
1.
A modified electrode was fabricated by means of electrodeposition nickel-nickel oxide and copper-cuprous oxide on a glassy carbon electrode in the solution of Ni2+ and Cu2+.
在含镍离子和铜离子的溶液中用循环伏安法在玻碳电极(GCE)表面电化学沉积一层镍-氧化镍及铜-氧化亚铜纳米粒子(Ni/NiO、Cu/Cu2O),在-0。
3) cuprous oxide
氧化亚铜
1.
Copper colloid oxidized by air to prepare cuprous oxide nanoparticles;
铜胶体氧化法制备纳米氧化亚铜
2.
Hydrothermal synthesis and growth mechanism of cuprous oxide microcrystals;
氧化亚铜微米晶的水热合成与生长机理
3.
Study of degradation of rhodamine B by cuprous oxide under solar light;
氧化亚铜可见光催化降解罗丹明B的初步研究
4) Cu_2O
氧化亚铜
1.
The Cu_2O/PPh_3/TBAB catalytic system was found to be efficient for the Sonogashira cross-coupling reaction.
在八面体型纳米氧化亚铜/PPh_3/TBAB催化体系催化下,卤代芳烃和卤代杂环芳烃与末端炔烃能够顺利反应,得到10%-98%的产率,而且催化体系重复使用4次,催化活性仍保持不变。
5) Cu2O
氧化亚铜
1.
Applying CuSO4,NaOH,C6H12O6 as raw materials,nano-sized Cu2O was synthesized by solid-state reaction at room temperature.
以硫酸铜、氢氧化钠、葡萄糖为原料,室温固相合成了纳米氧化亚铜粉体;利用X-射线衍射(XRD)和透射电子显微镜(TEM)对所得氧化亚铜粉体进行了表征;研究了在紫外光和太阳光下,所得氧化亚铜粉对甲基橙溶液的光催化降解效果。
2.
Results showed that the fracture was caused by higher content of O2,a large amount of Cu2O and residual stress.
结果表明,氧含量超标,存在大量的脆性相氧化亚铜,且材料内部仍留有部分残余应力,是失效的主要原因。
3.
Octahedron Cu2O crystal was prepared from CuSO4·5H2O and NaH2PO2 by homogeneous reduction.
5H2O和NaH2PO2为原料,采用化学还原法在均相体系中制备了八面体氧化亚铜晶体,其结构经IR,XRD和扫描电子显微镜表征。
6) oxygen content in copper
铜中氧含量
补充资料：氧化亚铜
Cu2O 分子量143．08
棕红色或暗红色结晶粉末。密度6．00g／cm3。熔点1235℃。沸点1800℃(失氧)。不溶于水和醇，溶于盐酸、氯化铵、氨水、浓碱、三氯化铁等溶液。干空气中稳定，湿空气中缓慢氧化成黑色氧化铜。有毒。
应用 用于制备船底防污漆，以杀死低级海生动物，对水平线以下的船体和船底起保护作用。用作陶瓷和搪瓷的着色剂，红色玻璃的染色剂。还用作有机硅树酯生产中，一氯甲烷与硅粉的加氢合成的催化剂。另外，还用于制造各种铜盐、分析试剂、杀菌剂以及在电器工业中用于整流电镀。
棕红色或暗红色结晶粉末。密度6．00g／cm3。熔点1235℃。沸点1800℃(失氧)。不溶于水和醇，溶于盐酸、氯化铵、氨水、浓碱、三氯化铁等溶液。干空气中稳定，湿空气中缓慢氧化成黑色氧化铜。有毒。
应用 用于制备船底防污漆，以杀死低级海生动物，对水平线以下的船体和船底起保护作用。用作陶瓷和搪瓷的着色剂，红色玻璃的染色剂。还用作有机硅树酯生产中，一氯甲烷与硅粉的加氢合成的催化剂。另外，还用于制造各种铜盐、分析试剂、杀菌剂以及在电器工业中用于整流电镀。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条