1) monomer casting
单体浇铸
1.
By using TG,the processes and kinetics of the thermal degradation of monomer casting nylon 6 in air surroundings have been studied.
通过热重分析研究了ＭＣ尼龙（单体浇铸尼龙）在空气环境下的热氧降解过程和降解动力学，选用ＭＣ尼龙粉粒为样品，应用日本ＴＡＳ－１００型热分析仪，升温速率分别为５℃／ｍｉｎ、１０℃／ｍｉｎ、１５℃／ｍｉｎ加热到５００℃，得到ＴＧ—ＤＴＧ的数据和曲线。
2) monomer cast nylon
单体浇铸尼龙
3) monomer cast polycaprolatam
单体浇铸聚己内酰胺
4) monomer casting polyamide 6
单体浇铸聚酰胺6
1.
Numerical simulation of cast-forming process and crystallization of Kevlar fiber reinforced monomer casting polyamide 6 was performed,the polymerization and crystallization heat were taken as internal heat sources in the finite difference method.
采用有限差分法,将聚合热和结晶潜热当作内部热源,对单体浇铸聚酰胺6/Kevlar纤维(KF)复合材料成型的聚合和结晶过程进行数值模拟。
5) Monoblock Casting
整体浇铸
1.
Monoblock Casting for the Large Bronze Buddhism Statue in Nepal Zhonghua Temple;
为解决处于浇注不利位置的头部易产生缺陷的课题 ,经研究分析 ,制定切合实际的工艺方案 ,在实践中获得成功 ,积累了大型佛像整体浇铸的经
6) casting matrix
浇铸体
1.
The relation of tensile strength,tensile modulus,flexural strength,flexural modulus and temperature of deflection of the epoxy resin casting matrix to the degree of cure is discussed.
采用DSC方法对低粘度环氧树脂基体进行了固化度分析,并研究了环氧树脂浇铸体的拉伸强度、拉伸模量、弯曲强度、弯曲模量和热变形温度与固化度之间的关系。
补充资料：单体浇铸尼龙
分子式：
CAS号：
性质：亦称铸型尼龙(cast nylon)。将己内酰胺(或其他内酰胺)熔融后加入催化剂和助催化剂，迅速均匀浇铸于预热的模具内，在惰性气体环境中使之开环聚合制得的浇铸制品。熔点198℃，拉伸强度75～97MPa，拉伸弹性模量240～310MPa，压缩强度96～104MPa，弯曲强度>95MPa，冲击强度(缺口)约5kJ/m2，洛氏硬度R95～120，热变形温度(0.45MPa)204～218℃。主要用于尼龙大型制品，少量多品种制品，如制作滑动轴承、齿轮、大型阀座、导轨、容器等。
CAS号：
性质：亦称铸型尼龙(cast nylon)。将己内酰胺(或其他内酰胺)熔融后加入催化剂和助催化剂，迅速均匀浇铸于预热的模具内，在惰性气体环境中使之开环聚合制得的浇铸制品。熔点198℃，拉伸强度75～97MPa，拉伸弹性模量240～310MPa，压缩强度96～104MPa，弯曲强度>95MPa，冲击强度(缺口)约5kJ/m2，洛氏硬度R95～120，热变形温度(0.45MPa)204～218℃。主要用于尼龙大型制品，少量多品种制品，如制作滑动轴承、齿轮、大型阀座、导轨、容器等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。