4) piezoelectric constant
![点击朗读](/dictall/images/read.gif)
压电常数
1.
At this sintering temperatures,the highest Curie temperature of the sample was 520℃,piezoelectric constant d_(33) was 9×10~(-12)C/N.
用溶胶-凝胶法制备了钛酸锶铋层状钙钛矿结构(SBTi)铁电陶瓷,研究了不同烧结温度对其显微结构和电性能的影响,分析了相关机理,发现1100℃烧结样品的晶粒发育比较完全,居里温度为520℃;压电常数d33和剩余极化强度2Pr较大,分别为9×10-12C/N和2。
2.
The piezoelectric constants d_(11) and d_(14) were determined to be 5.
![点击朗读](/dictall/images/read.gif)
室温时压电常数d11和d14分别为5。
3.
06TiO 3 ceramic, as its composition is near the morphotropic phase boundary (MPB), it shows the largest piezoelectric constant, d 33=173.
其中(Bi0 5Na0 5) 0 94 Ba0 0 6 TiO3系陶瓷具有该系列最大的压电常数 ,d33=173× 10 - 1 2 C N ,与传统工艺相比 ,d33提高了近4 0 % 。
6) piezoelectric coefficient
![点击朗读](/dictall/images/read.gif)
压电常数
1.
The Curie temperature and piezoelectric coefficient as well as piezoelectric voltage coefficient of lanthanum-modified Pb(1-x) Lax (Sc1/2Ta1/2)0.
03)陶瓷材料居里温度、压电常数及压电电压常数之间的关系以及高温热处理对材料性能的影响。
补充资料:弹性劲度常数
分子式:
CAS号:
性质:又称弹性劲度常数。弹性体在单位应力下发生的应变。是弹性体刚度的一种量度。通常用Cij表示,单位为Pa,由于压电体存在二极压电效应,在电学条件不同时,所测得的弹性刚度常数也不相同。在短路条件下测得的弹性刚度常数,称为短路弹性刚度常数,用表示。在开路条件下测得的弹性刚度常数,称为开路弹性刚度常数,用表示。弹性刚度常数共用10个,即、、、、和、、、和。压电陶瓷是弹性体,可用弹性刚度常数进行评价。弹性刚度常数值愈小,弹性体愈容易形变;其值较大,材料比较刚硬。
CAS号:
性质:又称弹性劲度常数。弹性体在单位应力下发生的应变。是弹性体刚度的一种量度。通常用Cij表示,单位为Pa,由于压电体存在二极压电效应,在电学条件不同时,所测得的弹性刚度常数也不相同。在短路条件下测得的弹性刚度常数,称为短路弹性刚度常数,用表示。在开路条件下测得的弹性刚度常数,称为开路弹性刚度常数,用表示。弹性刚度常数共用10个,即、、、、和、、、和。压电陶瓷是弹性体,可用弹性刚度常数进行评价。弹性刚度常数值愈小,弹性体愈容易形变;其值较大,材料比较刚硬。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条