1) pellicular resin
![点击朗读](/dictall/images/read.gif)
活化膜树脂
2) activated resin
![点击朗读](/dictall/images/read.gif)
活性化树脂
3) catalytic activated resin
![点击朗读](/dictall/images/read.gif)
催化活化树脂
1.
A new bonding system-catalytic activated resin normally used as the bonding agent of the carbon containing refractories is successfully developed in the recent years.
近来人们成功开发了1种催化活化树脂作为含碳耐火材料的结合剂。
4) activated carbonized resin support
![点击朗读](/dictall/images/read.gif)
活化炭化树脂
5) zinc oxide resin film
![点击朗读](/dictall/images/read.gif)
氧化锌树脂薄膜
6) Binder resin
![点击朗读](/dictall/images/read.gif)
成膜树脂
1.
In this paper,papers and patents about offset printing plates in recent years for binder resins and esterified resins were summarized.
对胶印版材所用的成膜树脂和阳图感光PS版用酯化树脂的相关文献进行了综述。
补充资料:环氧树脂活性稀释剂501
分子式:C7H14O2
分子量:130.19
CAS号:2426-08-6
性质:无色透明液体。相对密度0.915,沸点164℃,折光率1.420,闪点59℃。可溶于丙酮、苯、醇,不溶或难溶于水。
制备方法:由丁醇和环氧氯丙烷为原料,经两步反应合成。具体工艺过程为:将267kg丁醇和32kg浓度为96%的浓硫酸加入反应釜,搅拌,升温至55℃,滴加环氧氯丙烷324kg,温度控制在55-60℃约4h加完,再在60-65℃保温2h。然后,冷却至45℃,缓缓加入四氯化锡与丁醇的混合液(5kg四氯化锡溶于5kg丁醇中),再在60-65℃保温反应4h,反应完后,减压蒸馏回收未反应的环氧氯丙烷和丁醇,直至温度达到85-95℃,真空度93.1kPa下无环氧氯丙烷和丁醇蒸出为止。得到表氯醇丁基醚。将上述反应物料冷至30-35℃,滴加浓度30%的氢氧化钠432kg,约4h加完,然后升温至35-40℃并保温反应3h,再在搅拌下加入纯苯,升温至放掉盐水和碱水,然后水洗使pH约为6.5-7。放掉洗涤水,升温常压脱苯,直至料液温度达至140℃,然后冷却放料。两步总收率以丁醇计约为95%。
用途:该品可作双酚A环氧树脂的活性稀释剂。毒性小,使用方便。并能改善一些树脂硬化后的性能,如抗冲强度等。
分子量:130.19
CAS号:2426-08-6
性质:无色透明液体。相对密度0.915,沸点164℃,折光率1.420,闪点59℃。可溶于丙酮、苯、醇,不溶或难溶于水。
制备方法:由丁醇和环氧氯丙烷为原料,经两步反应合成。具体工艺过程为:将267kg丁醇和32kg浓度为96%的浓硫酸加入反应釜,搅拌,升温至55℃,滴加环氧氯丙烷324kg,温度控制在55-60℃约4h加完,再在60-65℃保温2h。然后,冷却至45℃,缓缓加入四氯化锡与丁醇的混合液(5kg四氯化锡溶于5kg丁醇中),再在60-65℃保温反应4h,反应完后,减压蒸馏回收未反应的环氧氯丙烷和丁醇,直至温度达到85-95℃,真空度93.1kPa下无环氧氯丙烷和丁醇蒸出为止。得到表氯醇丁基醚。将上述反应物料冷至30-35℃,滴加浓度30%的氢氧化钠432kg,约4h加完,然后升温至35-40℃并保温反应3h,再在搅拌下加入纯苯,升温至放掉盐水和碱水,然后水洗使pH约为6.5-7。放掉洗涤水,升温常压脱苯,直至料液温度达至140℃,然后冷却放料。两步总收率以丁醇计约为95%。
用途:该品可作双酚A环氧树脂的活性稀释剂。毒性小,使用方便。并能改善一些树脂硬化后的性能,如抗冲强度等。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。