1) loose ash
疏松灰
2) friable deposit
疏松沉积物，疏松积灰
3) loose deposit
疏松积灰，疏松结垢;疏松沉积物
4) saturated loose flyash
饱和疏松粉煤灰
5) porosity
[英][pɔ:'rɔsəti] [美][pɔ'rɑsətɪ]
疏松
1.
Effect of electric current pulse on shrinkage cavity and porosity in casting ZA27 alloy;
脉冲电流对铸造ZA27合金中缩孔和疏松的影响
2.
Factor Analysis and Countermeasures of Porosity and Pipe in Ingot;
钢锭疏松、缩孔的因素分析及对策
3.
In this paper, analysis on the fissuring accident of ZGMn13Cr2Mo antifriction tup is performed, and the reason is believed to lie in serious casting defects of shrinkage cavity, porosity and inclusion.
对ZGMn13Cr2Mo耐磨锤头的断裂事故进行了分析,主要原因是存在着严重的铸造缺陷:缩孔、疏松和夹杂物。
6) Looseness
[英]['lu:snis] [美]['lusnɪs]
疏松
1.
Results indicate that the primary cause to the rupture of the screw in the process of torque force test is proved to be heavily existence of holes and pore gaps in the screw arising from the central looseness of the original billet.
结果得出:螺钉在扭力试验过程中断裂是由于内部存在严重的孔洞和孔隙所造成的,孔洞和孔隙来源于原铸坯的中心疏松。
2.
Mechanism of central parosity and looseness of small billet is described and analysed.
简述小方坯中心缩孔和疏松的形成机理 ,提出减轻中心缩孔和疏松的措
3.
The experimental results show that there are some internal metallurgy flaws such as looseness,shrink hole in the raw material of the axle,and bad widmanstatten structure from the overheating and over-burning during the heating of forging,the comprehensive effects of these factors cause the steel toughness to reduce,and the internal cleavage exists d.
结果表明,车轴轴头原材料中存在疏松、缩孔残余等内部冶金缺陷和锻造热加工中的过热和过烧产生不良的魏氏组织,这些因素的综合作用致使钢的韧性降低,在锻造中发生内部劈裂,最终造成轴头在受外力时脆性断裂。
补充资料：粉煤灰硅酸盐水泥
分子式：
CAS号：
性质：由硅酸盐水泥熟料、粉煤灰、适量石膏磨细制成的水硬性胶凝材料，代号P·F，中国主要水泥品种之一。粉煤灰掺加量为20％～40％(wt)，标号分275、325、425、425R、525、525R、625R七个等级。性能和火山灰水泥相似，但需水性及干缩性较小，抗裂性较好，水化热较低，抗蚀性也较好。适用于一般的工业和民用建筑，尤其适用于大体积水工混凝土以及地下和海港工程等。
CAS号：
性质：由硅酸盐水泥熟料、粉煤灰、适量石膏磨细制成的水硬性胶凝材料，代号P·F，中国主要水泥品种之一。粉煤灰掺加量为20％～40％(wt)，标号分275、325、425、425R、525、525R、625R七个等级。性能和火山灰水泥相似，但需水性及干缩性较小，抗裂性较好，水化热较低，抗蚀性也较好。适用于一般的工业和民用建筑，尤其适用于大体积水工混凝土以及地下和海港工程等。