2) Hypercrosslinked resin
超高交联树脂
1.
Investigation on the removal of phenol-contained wastewater in 2,4-D production by hypercrosslinked resin;
超高交联树脂吸附处理2,4-D含酚废水的研究
2.
A hypercrosslinked resin (AM-1) has been synthesized and characterized.
合成和表征了超高交联树脂AM-1,以大孔吸附树脂AmberliteXAD-4为参照,比较研究了其在水溶液中吸附邻硝基苯酚,对硝基苯酚的吸附行为和热力学性质,测定了不同温度下的平衡吸附量,Langmuir模型和Freundlich模型均能很好拟合。
3.
The thermodynamic properties of hypercrosslinked resins AM-1 and macroporous adsorbent Amberlite XAD-4 in adsorption of aniline and 4-nitroaniline in aqueous solution have been studied under the static conditions.
研究了在静态条件下水溶液中超高交联树脂AM 1和大孔吸附树脂AmberliteXAD 4吸附苯胺和对硝基苯胺的热力学特性 ,测定了不同温度时的吸附等温线。
4) Hypercrosslinked polymeric adsorbent
超高交联吸附树脂
1.
Preparation and adsorption performance of hypercrosslinked polymeric adsorbents modified by phenolic hydroxyl group;
酚羟基修饰超高交联吸附树脂的制备与性能
2.
Using gelatin as dispersant,liquid paraffin as porogen,the novel hypercrosslinked polymeric adsorbent of LM-6 was prepared by post-crosslinking reaction with β-naphthol.
明胶为分散剂,液蜡为致孔剂,交联反应中溴乙烷代替有毒氯甲醚,以β-萘酚参与Friedel-Crafts后交联反应,成功制备了酚羟基修饰的超高交联吸附树脂LM-6。
5) hypercrosslinked polymeric resin
超高交联吸附树脂
1.
The adsorption thermodynamics of toluene onto new hypercrosslinked polymeric resins;
超高交联吸附树脂对有机物质甲苯的吸附热力学研究
6) hypercrosslinked polystyrene resin
高交联聚苯乙烯树脂
1.
The macroporous hypercrosslinked polystyrene resin synthesized in one step had many of carbonyl groups, which was indicated by the adsorption at 1704.
用一步法合成高交联聚苯乙烯树脂,采用红外光谱对其结构进行表征,其红外光谱图中在1704。
补充资料：苯二甲酸二烯丙酯交联不饱和聚酯树脂
分子式：
CAS号：
性质：以苯二甲酸二烯丙酯为交联剂形成的交联型不饱和聚酯。具有良好的耐热性、尺寸稳定性、耐水、耐候性。以邻苯二甲酸二烯丙酯为交联剂，通用型不饱和聚酯树脂为基料制得的玻璃钢制品，弯曲强度330.26MPa，体积电阻率1.9×1015Ω·cm。以苯乙烯为交联剂的弯曲强度280MPa，体积电阻率1.48×1014Ω·cm。先制成黏稠状的液体树脂，再加入10%～50%苯二甲酸二烯丙酯混溶后加工制得所需产品。可用作机械、电器用结构件和绝缘零部件。
CAS号：
性质：以苯二甲酸二烯丙酯为交联剂形成的交联型不饱和聚酯。具有良好的耐热性、尺寸稳定性、耐水、耐候性。以邻苯二甲酸二烯丙酯为交联剂，通用型不饱和聚酯树脂为基料制得的玻璃钢制品，弯曲强度330.26MPa，体积电阻率1.9×1015Ω·cm。以苯乙烯为交联剂的弯曲强度280MPa，体积电阻率1.48×1014Ω·cm。先制成黏稠状的液体树脂，再加入10%～50%苯二甲酸二烯丙酯混溶后加工制得所需产品。可用作机械、电器用结构件和绝缘零部件。