1) cadweld
铜与铜或铜与钢的铝热焊
2) spot-welding of aluminum and copper
铝铜点焊
1.
A method for spot-welding of aluminum and copper with a transition joint (a joint ithout potential difference) was put forward.
从而可利用热活化、压力、电磁搅拌力,使铝铜固溶,扩散和铝液面移动,完成铝铜点焊,获得比铝强度高的焊接接头,为铝代铜的运用提供了一种特殊的途径。
3) Al/Cu brazing
铝铜钎焊
1.
To realize and optimize Al/Cu brazing welding, and to resolve some problems of Al/Cu connection in air-condictioning and refrigeration industries, etc.
为实现和优化铜铝的钎焊连接,解决空调制冷等行业中铜铝焊接存在的关键工艺问题,本论文采用拉伸、DSC、SEM、EDS等实验方法系统研究了成分配比、合金元素、钎焊工艺对铜铝钎焊用Zn-Al钎料的性能和铝铜钎焊接头组织与性能的影响规律。
5) aluminum bronze-steel
铝青铜/钢
6) Cu-steel surfacing
铜钢堆焊
1.
A method combined with global and dynamic threshold image segmentation is proposed,and by which weak defect regions in the ultrasonic C-scan image of Cu-steel surfacing are segmented effectively.
采用全局阈值与动态阈值相结合的图像阈值化分割方法,较好地解决了铜钢堆焊接头超声检测图像中弱信号缺陷分割困难问题。
补充资料：铝-铜系铸造铝合金
分子式：
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。