1) upper bainite
上贝茵体
2) high bainite
上贝茵体，上贝氏体
3) lower bainite
下贝茵体
4) Bainite
['beinait]
贝茵体，贝氏体
5) Bain
贝茵
6) Upper bainite
上贝氏体
1.
The results show that the appearance of Widmanstatten structure,upper bainite and martensite in the structure of 20MnSi HRB is the main cause making the yield point disappear.
结果表明 :2 0 Mn Si热轧带肋钢筋中出现的魏氏组织、上贝氏体及马氏体组织是使屈服点消失的主要原因。
2.
The main reason why mechauical propcrties of qutnched and tem-Pered hcavy part or 35CrMo steel,such as impact toughness and so on,are impossiblc to meetthe requirements is regarded as tbe presentation or the upper bainite in its microstructure.
本文总结了多年来有关35CrMo钢热处理的经验，认为35CrMo钢制大件调质处理后冲击韧性等力学性能达不到要求的原因主要是组织中出现较大量的上贝氏体。
3.
The results show that upper bainite and grain boundary segregation of Si element result in embrittlement of the oil cylinder.
结果表明,上贝氏体和Si元素的晶界偏聚导致油缸变脆。
补充资料：贝茵体
分子式：
CAS号：
性质：又称贝茵体。钢中相形态之一。钢过冷奥氏体的中温(350～550℃)转变产物，α-Fe和Fe3C的复相组织。贝氏体转变温度介于珠光体转变与马氏体转变之间。在贝氏体转变温度偏高区域转变产物叫上贝氏体(up bai-nite)，其外观形貌似羽毛状，也称羽毛状贝氏体。冲击韧性较差，生产上应力求避免。在贝氏体转变温度下端偏低温度区域转变产物叫下贝氏体。其冲击韧性较好。为提高韧性，生产上应通过热处理控制获得下贝氏体。
CAS号：
性质：又称贝茵体。钢中相形态之一。钢过冷奥氏体的中温(350～550℃)转变产物，α-Fe和Fe3C的复相组织。贝氏体转变温度介于珠光体转变与马氏体转变之间。在贝氏体转变温度偏高区域转变产物叫上贝氏体(up bai-nite)，其外观形貌似羽毛状，也称羽毛状贝氏体。冲击韧性较差，生产上应力求避免。在贝氏体转变温度下端偏低温度区域转变产物叫下贝氏体。其冲击韧性较好。为提高韧性，生产上应通过热处理控制获得下贝氏体。