1) transgranular stress corrosion cracking
穿晶应力腐蚀开裂
2) transgranular stress corrosion cracking
穿晶应力腐蚀裂缝
3) corrosion crack
腐蚀裂纹，应力腐蚀裂纹;晶间开裂
4) Intergranular stress corrosion cracking
晶间应力腐蚀开裂
5) IGSCC
沿晶应力腐蚀开裂
1.
However,laboratory tests and field experience indicates the 13 Cr steel undergoes inter-granular stress corrosion cracking(IGSCC) in the heat affected zone of the welds.
但是实验室试验和现场经历表明,13Cr马氏体不锈钢焊接接头热影响区发生了沿晶应力腐蚀开裂(IGSCC)。
6) stress corrosion crack
应力腐蚀开裂
1.
On behavior of sulfide-stress corrosion cracking (SSCC) of X80 pipeline in H_2S environment;
X80焊管H_2S环境应力腐蚀开裂行为研究
2.
The stress corrosion crack causes of high sulfur pipes serviced hydrodesulfurization system of a refinery were analyzed.
表明管道的开裂是由富含H_2S环境介质再加上焊缝附近较高的焊接残余应力引起的应力腐蚀开裂。
3.
The susceptibility to stress corrosion cracking (SCC) of the welded joint of X80 pipeline steel in solution of 0.
5mol/LNa2CO3+1mol/LNaHCO3溶液中的应力腐蚀开裂(SCC)敏感性。
补充资料：晶间开裂
分子式：
CAS号：
性质： 金属材料破裂的金属学特征之一，裂纹沿晶粒之间的界面扩展。表征材料发生了脆性断裂，断口微观特征为“冰糖”状、岩石状。在材料的低温脆断、应力腐蚀破裂和氢脆破裂中经常能观察到晶间开裂。
CAS号：
性质： 金属材料破裂的金属学特征之一，裂纹沿晶粒之间的界面扩展。表征材料发生了脆性断裂，断口微观特征为“冰糖”状、岩石状。在材料的低温脆断、应力腐蚀破裂和氢脆破裂中经常能观察到晶间开裂。