1) solid solution range
固溶体区域
2) solid solution
固溶区
1.
The solid solution and crystal structure of Pr_(1+x)Ba_(2-x)Cu_3O_(7±8) were investigated by means of X-ray powder diffraction combined with Rietveld analysis.
Pr_(1+x)Ba_(2-x)Cu_3O_(7±δ)固溶区的范围为0。
2.
The particle size, morphology, valence, solid solution range, phase relations and magnetic properties of Ti_ 1-x Cr_xO_ 2±δ samples were studied by XRD, SEM, XPS and SQUID measurements.
利用扫描电子显微镜(SEM),X射线光电子能谱(XPS),粉末X射线衍射分析(XRD)方法研究了Ti1-xCrxO2±δ系列样品的颗粒尺寸、形貌、组分化学态、相关系和固溶区范围;并利用超导量子干涉磁强计对样品的磁性能进行了研究。
3.
The morphology,phase relations and solid solution range of Y(1-x)LuxMnO3 samples were studied by XRD and SEM.
利用粉末X射线衍射分析(XRD)和扫描电子显微镜(SEM),研究了Y(1-x)LuxMnO3体系的样品形貌、相关系和固溶区范围。
3) solubilized region
增溶区域
5) solid solution
固溶体;固体溶液
6) reinforcing area
加固区域
1.
A method for the quality test of reinforcing areas in concrete components is provided in this paper, which is proved effective and accurate in aspects of strength and density test through application.
本文提出了混凝土构件加固区域质量检测的方法,并结合实际工程验证了采用该方法检测混凝土构件加固区域质量的准确性,包括检测强度、密实性及结合面质量的准确性。
补充资料：固溶
固溶
solid solution
gUrong 固溶(solid solution)两种或两种以上的物 质相互溶解生成固溶体的现象。固相间的相互溶解有 完全互溶型和有限互溶型两大类，前者生成连续固溶 体，后者生成有限固溶体，在衬火材并中这两种类型都 存在，例如Mgo，Feo、MgO一Fe:03、MgO一AI:03、Mgo- crZo:和M扣一CaO系统等。作为杂质的固相(溶质) 固溶到主晶相(溶剂)中，必然使主晶相的熔融温度下 降，并且随固溶度的增大而增加，这是不利的一面，但 它作为与主晶相不互溶而形成简单低共熔混合物的杂 质相来说，则有利得多。以MgO~Feo为例，如在MgO- FeO二元系内不生成固溶体，则在二者之间必产生共 熔点，共熔点温度必低于两个端元的熔点，即低于 Mgo、Feo的熔点，实际上，M四一Feo二元系内不产 生共溶点;而产生连续固溶体，最低产生液相的温度在 端元中的最低熔点(1360℃—FeO的熔点)之上。以---一-一，一上两种情况对比见图。由图中看出，后者的始熔比前者\一二、一 M凶/%FeO一M扣z%Mg(、 a吞 MgO一FeO系相图 a一假设的M四一氏O系的共熔点.卜一M扣子州O二元系相平衡圈 ;提高了，这是固溶体对耐火材料的高锰力学性质及抗 渣性能的一大贡献.此外，由于杂质相在主晶相的固溶 形成固溶体，使主晶相晶格变形，点阵块陷增加，能t !升高，有利于离子扩散与烧结的进行，所以在耐火材料 中，选择与主晶相能形成固溶体的少t添加物(杂质 :相)作为促进烧结的矿化剂，可应用以上机理得到解 释，如钱砂生产中加入Fe:O:所起的作用就是一个例 }子。 l(张垂昌)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。