1) soft facing
软堆焊
2) hardfacing
堆焊
1.
Wear resistant impact hardfacing flux-cored wire used in tool manufacture of shield machine;
盾构机刀具制造用耐磨耐冲击堆焊药芯焊丝的研究
2.
Effect of alloy elements and heat treatment technology on microstructure and property of hardfacing metal for cold scissors;
冷剪刃堆焊金属的组织与性能
3.
Field mobile welding machine for drilling tool hardfacing;
野外可移动式钻具耐磨带堆焊专机
3) surfacing
[英]['sə:fis] [美]['sɝfɪs]
堆焊
1.
Effect of welding material component on high frequency surfacing process;
焊料成分对高频堆焊性能的影响
2.
Ultrasonic signal character and quality evaluation of Cu/steel surfacing weld;
铜钢堆焊接头的超声信号特征及质量评价
4) surfacing welding
堆焊
1.
Development of special welding machine for inner surfacing welding of high-temperature cylinder;
高温圆筒内壁堆焊焊接专机的研制
2.
Automatic surfacing welding method with equal thickness for circle plane;
一种圆环面等厚自动堆焊方法
3.
Research on new technology of repairing rails tracks by surfacing welding;
铁路在线伤损钢轨堆焊修复新技术研究
5) build-up welding
堆焊
1.
The process of Ni-alloy build-up welding to improve the valve's sealing face was introduced.
详细介绍了一种改善旋转止回阀密封面性能的镍基堆焊工艺。
2.
Combined with specific experiences, it carries out chemical analysis for base metal of sprocket in drive gear, checks surface heat processing state, its welding capacity is also analyzed, and introduces specific build-up welding technology, the effect is good through test.
结合具体的工程实践,对提升机传动机构中链轮的母材进行了化学分析,对表面热处理状态进行了检测,并对堆焊齿形的可焊性作了分析,介绍了具体的堆焊工艺,经试用,效果良好。
3.
Withdrawal roll and wrapper rolls were strengthened by build-up welding against their short- life,using PYY125 tube welding wire+SSD welding flux as build-up welding materials.
针对夹送辊和助卷辊的使用寿命低的现状 ,选择PYY 12 5管状焊丝 +SSD焊剂作为堆焊材料 ,采用合适的堆焊工艺对夹送辊和助卷辊进行堆焊 ,经现场使用 ,其过钢量分别达到 2 6 。
6) overlaying welding
堆焊
1.
Relationship between characterization of interface of overlaying welding and crackle forming;
堆焊层的界面特征与裂纹形成的关系
2.
Taking Fe_3Al as welding wire,overlaying welding was conducted on austenite stainless steel using gas arc tungsten welding process.
以Fe_3Al合金为焊丝,用钨极氩弧焊在不锈钢基体上进行堆焊,采用静态增重法测定堆焊层在850℃、950℃、1050℃和1150℃时的氧化动力学曲线。
3.
Arc-ultrasonic was successfully induced in the process of overlaying welding and thermal spraying.
将电弧超声引入堆焊和热喷涂工艺,进行常规堆焊、等离子喷涂和引入电弧超声技术的对比试验,比较其堆焊层的金相组织、硬度、抗弯性能、冲击韧度和热障涂层的孔隙率、抗热震性能,结果表明:电弧超声的加入能够细化堆焊接头的熔合区组织,降低脆硬倾向,改善堆焊接头的抗弯性能和冲击韧性;由于超声波的空化效应、热效应和机械效应,电弧超声改善了喷涂过程的雾化效果,减小了熔滴的颗粒度和涂层中弥散气孔的尺寸,提高了热障涂层的抗热震性能。
补充资料：堆焊
在金属零件表面熔敷耐磨、耐腐蚀或其他特殊性能的金属层的焊接方法。堆焊层可显著改善工件的工作性能或提高其使用寿命，还可以节约贵重金属材料，降低生产成本。常用的堆焊材料有各种钢、合金铸铁、镍基合金、钴基合金和铜合金，以及碳化钨与适当基体金属组成的复合材料等。堆焊材料根据工件工作时的磨损类型、介质性质和工作温度来选择。堆焊材料按其加工性能的不同可以轧成丝或带，铸成条或制成粒状粉末，制成药芯焊丝或涂药焊条。几乎所有的熔化焊工艺方法都可以用于堆焊，但应尽可能选用母材熔深较浅、填充材料熔化较快、经济性好的工艺方法。常用的有手工电弧堆焊、丝极或带极埋弧堆焊和等离子弧堆焊等。堆焊广泛用于在钢制工件上熔敷各种金属和合金，例如在原子能压力容器内壁堆焊不锈钢，在高炉料钟表面堆焊高铬合金铸铁，在热轧辊表面堆焊热模具钢，在柴油机排气阀表面堆焊镍基或钴基合金，以及在机械修理中修复各种被磨损的轴等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。