1) eutectic trough
共晶谷
2) eutectic valley
共晶谷
3) eutectic
共晶
1.
Multiphase field simulation of the eutectic growth under three schemes of varying velocity;
三种变速条件下共晶生长的多相场法模拟
2.
Preparation of Lotus-type Porous Metal with Metal-gas Eutectic Directional Solidification;
金属-气体共晶定向凝固制备藕状多孔金属的研究
3.
Research and Application of Vacuum Eutectic Technology;
真空共晶技术的研究应用
4) eutectics
共晶
1.
The criteria for stability of eutectics,solid solutions and precipitates are proposed.
本文是Thomas-Fermi-Dirac-Cheng电子理论对共晶机理的阐述。
5) co-crystallizing
共晶
6) eutecticum
共晶
7) hypoeutectic
亚共晶;亚共晶的
8) hyper-eutectic
过共晶的;过共晶
9) Eutectic structure
共晶组织
1.
Effects of Cooling Rate on Eutectic Structure of Zn-0.24Ni Alloy;
冷却速度对Zn-0.24Ni合金共晶组织的影响
2.
Besides,microscopic structure is eutectic structure of γ-.
结果表明:该涂层与基体呈冶金结合,内部组织均匀细密无缺陷,是固溶了大量Cr的-γFe相与高硬度析出相的共晶组织;其在海水中的耐蚀性远高于0Cr18Ni9Ti不锈钢,两者在海水中均表现为点蚀。
3.
The results show that some defects such as metallic inclusion,unmerited heat treatment process and so on,conduce the existence of bulky acicular silicon and herringbone(α+Si) two-phase eutectic structure,which reduces the mechanical properties.
结果表明,轮辋材质成分夹杂、热处理工艺不当等缺陷造成组织中存在大量的粗针状硅和鱼骨状(α+Si)两相共晶组织,该组织降低其力学性能是造成轮辋脆性断裂失效的主要原因。
10) eutectic Si
共晶Si相
1.
The effect of the solidified rate on the morphology of eutectic Si and α-Al dendrite was studied by mean of scanning electron microscope(SEM).
利用扫描电子显微镜,研究凝固速度对共晶Si相、α(Al)树枝晶形态的影响。
补充资料：共晶
共晶
eutectic
共晶eutectic一定成分的合金液体冷却时，转变为两种或更多紧密混合的固体的恒温可逆反应。这种反应形成的组织即为共晶组织。最简单的共晶反应是在二元合金系统中，具有共晶成分的液体L，在共晶温度下同时凝固形成两固体相a和刀共晶组织。通常用公式L禅a+刀表示。在此共晶反应温度下，出现L、a及刀三相共存。以此方式凝固的合金为共晶合金。偏离共晶成分的合金组织为亚共晶或过共晶。在冷却过程中，这些合金首先从液体中析出树枝状的先共晶组织，然后在枝晶间的液体凝固成共晶组织。可通过高的冷却速度或在液固界面高的温度梯度来抑制先共晶组织的形成，使液体可以直接通过共晶方式凝固;并可调节a及刀相的体积分量与液体的成分相适应。通常这种共晶组织又称为伪共晶。 共晶合金由于熔点低，熔化工艺相对比较简单，并且成本亦低。由于凝固的温度范围很小，改善了铸造流动性，并可抑制热缩孔、疏松及成分偏析。共晶合金具有细而分隔的多相显微组织，可以认为是具有各种特殊性能的复合材料。根据此原理，已开发出镍基和钻基共晶合金，用作抗蟠变材料，可制作喷气发动机叶片。 (汪复兴)