2) eutectic composition
共晶组成
1.
The eutectic compositions of the ZrO 2-mullite system in fused material were studied by mean of SEM-EDAX.
按统计结果共晶组成为 (质量分数 ,% ) :Al2 O35 3。
3) Composed-crystal
共晶合成
1.
Application of Kingview in the Composed-crystal Monitoring System;
Kingview在共晶合成监控系统的应用
4) eutectic component Mg-Al alloy
共晶成分镁铝合金
5) eutectic fraction
共晶分数
1.
The solidification path and eutectic fractions were obtained by employing the binary partition coefficient and CALPHAD technology separately.
实验发现三元合金中溶质分凝因数在凝固过程变化巨大 ,采用二元系中的参数使得对共晶种类和共晶分数的预测均与实验值有较大偏差。
6) separated eutectic
分离共晶
1.
Based on the formation of separated eutectic during electromagnetic stirring and unidirectional solidification, composite materials was prepared which was composed of hypo eutectic matrix and composite surface such as pure Si or inter metallic compound Al3Fe, Al3Ni, Al6Mn.
根据电磁搅拌下定向凝固时形成分离共晶的原理，制备了表面为 Ｓｉ和 Ａｌ３Ｆｅ，Ａｌ３Ｎｉ， Ａｌ６Ｍｎ等金属间化合物的表面复合材料。
2.
The separated eutectic for nearly 20 kinds of simple and complex eutectic alloys was investigated.
研究了近２０种简单和复杂二元共晶合金在强磁场搅拌下形成分离共晶的现象。
补充资料：共晶
共晶
eutectic
共晶eutectic一定成分的合金液体冷却时，转变为两种或更多紧密混合的固体的恒温可逆反应。这种反应形成的组织即为共晶组织。最简单的共晶反应是在二元合金系统中，具有共晶成分的液体L，在共晶温度下同时凝固形成两固体相a和刀共晶组织。通常用公式L禅a+刀表示。在此共晶反应温度下，出现L、a及刀三相共存。以此方式凝固的合金为共晶合金。偏离共晶成分的合金组织为亚共晶或过共晶。在冷却过程中，这些合金首先从液体中析出树枝状的先共晶组织，然后在枝晶间的液体凝固成共晶组织。可通过高的冷却速度或在液固界面高的温度梯度来抑制先共晶组织的形成，使液体可以直接通过共晶方式凝固;并可调节a及刀相的体积分量与液体的成分相适应。通常这种共晶组织又称为伪共晶。 共晶合金由于熔点低，熔化工艺相对比较简单，并且成本亦低。由于凝固的温度范围很小，改善了铸造流动性，并可抑制热缩孔、疏松及成分偏析。共晶合金具有细而分隔的多相显微组织，可以认为是具有各种特殊性能的复合材料。根据此原理，已开发出镍基和钻基共晶合金，用作抗蟠变材料，可制作喷气发动机叶片。 (汪复兴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。