2) Be-Al alloy
铍铝合金
1.
Finite element simulation of tensile properties in powder metallurgy Be-Al alloy
粉末冶金铍铝合金拉伸性能的有限元模拟
2.
The results show that Be-Al alloy has satisfying tensile properties at room temperature and the tensile behaviors are sensitive to the strain speed.
通过室温拉伸试验和SEM原位疲劳测试,研究了金属型复合材料铍铝合金的拉伸性能及拉伸和原位疲劳的断裂机制。
3.
The effect of different content of beryllium and aluminum on the microstructure,mechanical properties of the powder metallurgy Be-Al alloy was studied by means of mechanical tensile test at room temperature and SEM analysis.
通过室温拉伸试验和扫描电镜观察与分析,研究不同铍铝配比对粉末冶金铍铝合金的显微组织和力学性能的影响。
3) different content of beryllium and aluminum
铍铝配比
1.
The effect of different content of beryllium and aluminum on the microstructure,mechanical properties of the powder metallurgy Be-Al alloy was studied by means of mechanical tensile test at room temperature and SEM analysis.
通过室温拉伸试验和扫描电镜观察与分析,研究不同铍铝配比对粉末冶金铍铝合金的显微组织和力学性能的影响。
4) beral coating
铍铝镀层
6) beryllium aluminate
铝酸铍BeO. Al2O3
补充资料：铍铝合金
分子式：
CAS号：
性质：一种含铝铍基合金。一般含铝25%～43%（质量）。密度2.10g/cm3。有LX-62和LX59-3两种牌号。抗拉强度524～670MPa，屈服强度479～516MPa，伸长率3.7%～4.3%。采用粉末冶金挤压、轧制工艺生产。用于导弹、火箭、超高速结构件、飞机制动器和电子计算机磁盘驱动器。
CAS号：
性质：一种含铝铍基合金。一般含铝25%～43%（质量）。密度2.10g/cm3。有LX-62和LX59-3两种牌号。抗拉强度524～670MPa，屈服强度479～516MPa，伸长率3.7%～4.3%。采用粉末冶金挤压、轧制工艺生产。用于导弹、火箭、超高速结构件、飞机制动器和电子计算机磁盘驱动器。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。