1) SCC
应力-腐蚀破裂
2) stress corrosion cracking
应力腐蚀破裂
1.
Alkali cleaning and stress corrosion cracking in petrochemical equipment;
石化设备碱洗与应力腐蚀破裂
2.
The effect of micro-alloying elements on the behavior of stress corrosion cracking of the weld metal;
微合金元素对焊缝金属应力腐蚀破裂性能的影响
3.
Progress in the research on stress corrosion cracking of dental casting alloys;
齿科铸造合金应力腐蚀破裂的研究进展
3) SCC
应力腐蚀破裂
1.
SCC initiated from outside surface and induced by chloride ions was the main failure reason.
通过对盐酸塔不锈钢壳体的化学成分、金相、断口、介质等分析,寻找产生裂纹的原因,外壁氯离子环境造成的应力腐蚀破裂(SCC)是不锈钢失效的主要原因,对此提出采取对下部壳体外壁喷涂环氧树脂,以隔断腐蚀介质的侵蚀,3年来使用情况良好。
2.
The SCC behavior of 316 stainless steel in high temperature water containing 5ppm Cl~- at 300℃ was studies using slow strain rate tests.
采用慢应变速率试验(SSRT)技术研究了固溶态的和敏化态的316型不锈钢在含5ppm Cl~-的300℃高温水中子不同电位下的应力腐蚀破裂(SCC)行为,并对SCC试样表面膜进行了俄歇电子能谱(AES)分析。
3.
The influence of water stabilizer Rp-04L on stress corrosion cracking (SCC) of 304 stainless steel was investigated in simulated hard cooling water by means of electrochemical tests under constant strain and slow strain rate tests (SSRT).
结果表明:水质稳定剂Rp-04L对304不锈钢在高硬度循环冷却水中的应力腐蚀破裂有明显的抑制作用。
4) stress corrosion cracking(SCC)
应力腐蚀破裂(SCC)
5) HSCC
氢应力腐蚀破裂
6) stress corrosion cracking
应力腐蚀裂缝，应力腐蚀裂纹，应力腐蚀破裂
补充资料：连多硫酸应力腐蚀破裂
分子式：
CAS号：
性质：奥氏体不锈钢应力腐蚀破裂的一种类型。主要发生在接触高温含硫介质的化工装置中。在高温下钢表面生成硫化铁，当装置停车时温度降低，硫化铁与水分和空气相接触，反应生成连多硫酸H2SxO6(x=3，4，5)，导致不锈钢发生晶间型应力腐蚀破裂。抗晶间腐蚀性能较好的钢种，其抗连多硫酸应力腐蚀破裂的性能也较好。
CAS号：
性质：奥氏体不锈钢应力腐蚀破裂的一种类型。主要发生在接触高温含硫介质的化工装置中。在高温下钢表面生成硫化铁，当装置停车时温度降低，硫化铁与水分和空气相接触，反应生成连多硫酸H2SxO6(x=3，4，5)，导致不锈钢发生晶间型应力腐蚀破裂。抗晶间腐蚀性能较好的钢种，其抗连多硫酸应力腐蚀破裂的性能也较好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。