1) knife-line attack
刀线腐蚀
2) knife line attack
刀状腐蚀
1.
The problem of the knife line attack of welded joint is soluted,the life of welding impeller made of Cr17Ni2 steel is prolonged and it gets evident economical benefit.
采用二次稳定化退火处理 ,解决了 Cr17Ni2钢异质焊接接头刀状腐蚀的问题。
3) knife corrosion
刀口腐蚀
4) knife-line attach
刀切状腐蚀
6) corrosion wire breakage
腐蚀断线
1.
In order to solve the new contradiction and questions about lightning strike breakdown,insulation coordination,equipment selection,construction technology caused by overhead line distribution net newly built using the insulated conductor and old line insulation transformation,the article analyses thoroughly mechanism on lightning strike breakdown and corrosion wire breakage.
针对新网架空线路采用的绝缘导线和老线路的绝缘化改造带来的雷击断线及绝缘配合、设备选型及施工工艺等方面的新矛盾及问题,论文深入分析了雷电断线和腐蚀断线的机理,对比目前所采取技术手段的优缺点,结合线路现状,提出了采用过电压保护器进行改造的方法,详细论述了过电压保护器设备的选择和设备参数的选取,提出相应施工及技术改进措施。
补充资料：刀状侵蚀
分子式：
CAS号：
性质：晶间腐蚀的一种类型，主要发生于含钛或铌的奥氏体不锈钢焊接件上。腐蚀区域紧邻焊缝，窄而深，状如刀口。焊接后对工件进行1050℃固溶处理可以防止。
CAS号：
性质：晶间腐蚀的一种类型，主要发生于含钛或铌的奥氏体不锈钢焊接件上。腐蚀区域紧邻焊缝，窄而深，状如刀口。焊接后对工件进行1050℃固溶处理可以防止。