1) cyclododecalactam
环十二烷内酰胺
2) laurolactam
十二内酰胺
1.
Study on MC Nylon Modified with Laurolactam;
十二内酰胺改性铸型尼龙的研究
2.
Cast nylon modified with laurolactam was prepared by activated anionic copolymerization under the adiabatic condition.
在绝热条件下通过活化阴离子共聚制备十二内酰胺改性浇铸尼龙,对其力学性能进行了研究。
3.
In this paper the synthetic method for MC nylon modified with laurolactam is presented.
介绍了十二内酰胺改性铸型尼龙的制备方法 ,在绝热条件下通过活化阴离子共聚制得己内酰胺与十二内酰胺共聚体 。
3) dodecyl amide
十二烷基酰胺
4) N-[3-(dimethyloxidoamino)propyl]-Dodecanamide
N-[3-(二甲基环氧氨基)丙基]十二烷酰胺
5) polydodecalactam
聚十二内酰胺
1.
The CIIR/polydodecalactam 12(PA12) thermoplastic vulcanizate(TPV) was prepared by dynamic vulcanization,the influence of blend ratio,the addition level of curing agent,the compatibilizer species and dynamic vulcanization process on the physical properties,rheological behaviour and air permeability of CIIR/PA12 TPV were investigated.
采用动态硫化方法制备CIIR/聚十二内酰胺(PA12)热塑性硫化胶(TPV),研究CIIR/PA12共混比、硫化剂用量、相容剂品种和动态硫化加工工艺对CIIR/PA12 TPV物理性能、流变性能和气密性的影响。
6) aziridin-2-one
内酰胺环丙烷
补充资料：环十二烷
分子式：C12H24
分子量：168.32
CAS号：294-62-2
性质：无色结晶。熔点60-61℃，沸点118℃（2.40kPa），相对密度0.871（20/4℃）。
制备方法：1.环十二碳三烯加氢制取。也可由石油裂解所得C4馏分中的1,3-丁二烯直接进行三聚成环十二碳三烯，再经加氢而得。加氢所用催化剂为骨架镍，在压力1.961-2.941MPa、反应温度80-100℃条件下进行。整个反应过程较长，操作复杂。2.以环十二酮为原料，用锌汞齐和盐酸进行还原制得。
用途：有机中间体，用作尼龙的单体、十二内酰胺的中间体。
分子量：168.32
CAS号：294-62-2
性质：无色结晶。熔点60-61℃，沸点118℃（2.40kPa），相对密度0.871（20/4℃）。
制备方法：1.环十二碳三烯加氢制取。也可由石油裂解所得C4馏分中的1,3-丁二烯直接进行三聚成环十二碳三烯，再经加氢而得。加氢所用催化剂为骨架镍，在压力1.961-2.941MPa、反应温度80-100℃条件下进行。整个反应过程较长，操作复杂。2.以环十二酮为原料，用锌汞齐和盐酸进行还原制得。
用途：有机中间体，用作尼龙的单体、十二内酰胺的中间体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。