1) armourplate glass
钢化玻璃板
2) GFRP plate
玻璃钢板
1.
The regularity of interface stress with the differ of differ of length and thickness of GFRP plates.
对玻璃钢板加固既有混凝土梁界面应力进行了理论计算和有限元分析,研究了不同玻璃钢板长度、厚度对界面应力的影响,得到了界面应力随玻璃钢板长度、厚度变化的规律。
2.
After prestressed Glass-Fibre-Reinforced-Polymer(GFRP) plates were bonded on the tension face of RC beams,two distributing kinds of GFRP plates were bonded on the sides of the beams to improve shear capacity of RC beams.
先通过预张玻璃钢板(Glass-Fibre-Reinforced-Polymer,简称GFRP)粘贴于混凝土梁受拉面,后在梁侧面用GFRP板进行剪切补强试验;分析了不同侧面贴GFRP方式对加固梁抗剪性能和破坏模式的影响,比较了各试验梁的跨中挠度、力筋和GFRP板应变的关系。
3.
The regularity of interface stress varying from d ifferent length and thickness ofGFRP plates is given.
本文对玻璃钢板加固混凝土梁界面应力进行了有限元分析,研究了不同玻璃钢板长度、厚度对界面应力的影响,得到了界面应力随玻璃钢板长度、厚度变化的规律。
3) GFRP plates
玻璃钢板
1.
Several problems in the concrete beams strengthened with GFRP plates;
玻璃钢板加固既有混凝土梁应注意的问题
2.
The deflection influenced by different length and thickness of GFRP plates is investigated, and the regularity of deflection with different length and thickness of GFRP plates is obtained, which provides basis for displacement calculation of reinforced concrete beams.
对玻璃钢板加固混凝土的挠度进行了试验研究和有限元分析,研究了不同玻璃钢板长度、厚度对挠度的影响,得到了挠度随玻璃钢板长度、厚度变化的规律,为加固梁的变形计算提供依据,有限元计算结果与试验结果吻合较好。
4) glass toughening
玻璃钢化
5) Tempered Glass
钢化玻璃
1.
It has been discovered and demonstrated, via scanning electron microscope examination on 6 samples of broken glasses, that one important cause for the spontaneous breakage in tempered glass occurs as a result of the single-phase polycrystalline silicon particles, rather than simply the nickel sulfide (NiS) particles that are commonly recognized to be the main cause for the spontaneous breakage.
通过对 6 块玻璃自爆残片的电镜观察和成分分析,发现并证明了引起钢化玻璃自爆的主要原因不仅仅是传统认识中的硫化镍(NiS)微粒,很多情况是由单质硅微粒引起的。
2.
The causes of bend and distortion of tempered glass were discussed and some solutions were also suggested under any circumstances.
分析了钢化玻璃变形弯曲的原因,提出了各种情况下解决钢化变形的方法。
3.
Beijing Botanical Garden Exhibition Greenhouse uses point type glass curtain wall with imported tempered glass from French.
北京植物园展览温室采用点式玻璃幕墙 ,其钢化玻璃均从法国进口 ,抗弯强度和弹性模量能否采用现有的中国幕墙规范数值是个问题。
6) toughened glass
钢化玻璃
1.
Experimental study on the effect of toughened glass protected by window type sprinkler;
窗型玻璃喷头对钢化玻璃保护效果的实验研究
2.
Experimental study on the effect of single-pane toughened glass protected by water sprinkler as fire barrier;
喷水保护单片钢化玻璃作为防火分隔的有效性实验研究
3.
The article describes the problem of the toughened glass' surface defect and the method of prevention and solution.
针对钢化玻璃表面质量存在的变形点缺陷,采取相对应措施预防和解决。
补充资料：钢化玻璃
| 钢化玻璃 toughened glass 经强化处理、具有良好机械性能和耐热振性能的玻璃制品。主要用于汽车、火车、船舶、建筑物、器皿、仪表、家具等方面。钢化玻璃的制作工艺可以分为物理钢化和化学钢化两大类。物理钢化是将玻璃加热到接近软化温度，随即用冷却介质快速冷却，使玻璃表面产生压应力。按其冷却介质的不同，可以分为风冷钢化、液冷钢化和固冷钢化。其制品有平钢化玻璃、弯钢化玻璃、半钢化玻璃、区域钢化玻璃、器皿钢化玻璃、仪表用钢化玻璃等。物理钢化玻璃具有较高的抗弯强度、抗冲击强度和抗热振性能，破碎后，其碎片不带尖锐棱角，而是聚在一起成为布满裂缝的集合体，可减少对人的伤害。但物理钢化玻璃不能进行机械切割和钻孔，有自爆等特性。化学钢化是用化学方法改变玻璃表面组分以增加玻璃机械强度和耐热振性。其工艺过程是：在一定温度下，把玻璃浸入熔盐中，玻璃中的碱离子与熔盐中的碱离子因扩散而发生离子交换，使玻璃表面产生压应力，从而提高玻璃的机械强度和抗热振性能。可分为低温和高温两种类型，适用于薄壁、异型和要求尺寸精确的玻璃制品。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。