2) Layered forming
分层成形
3) coating formation
涂层形成
1.
Simulation of coating formation during plasma spraying;
等离子体喷涂中涂层形成的模拟
4) cambium
[英]['kæmbiəm] [美]['kæmbɪəm]
形成层
1.
Development and activity periodicity of cambium in Camptotheca acuminata;
喜树形成层的发育及周年活动
2.
The influences of several biochemical substance in cambium of grafted trees were investigated to reveal the survival mechanism of grafting.
为了研究大扁杏嫁接部位形成层相关生化物质含量变化对其成活的影响,探讨杏树嫁接成活机理。
3.
In Eucommia ulmoides , the cambium reactivated at the last ten days of March when buds were sprouting and produced secondary xylem and phloem.
杜仲形成层在３月下旬芽开始绽开时恢复活动，同时产生木质部和韧皮部。
5) Procambium
[英][prəu'kæmbiəm] [美][pro'kæmbiəm]
原形成层
1.
from procambium to cambium in the field of developmental anatomy.
作者对刺桐原形成层向维管形成层转化的研究表明 ,刺桐的维管形成层为叠生形成层 ,由分散的、排列成环的原形成层束转化而来 ,其转化过程是渐进的 。
2.
Observations were made on the process of transition from procambium to camhiumin the shoots of Camptotheca acuminata Decne.
观察了枣树茎中原形成层到形成层的转化过程。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。