疏松结构,loose structure,在线英语词典,英文翻译,专业英语

1) loose structure

疏松结构

2) gassy surface

疏松结构

3) fuzzy texture

疏松结构(搪瓷)

4) porosity

疏松

Effect of electric current pulse on shrinkage cavity and porosity in casting ZA27 alloy;

脉冲电流对铸造ZA27合金中缩孔和疏松的影响

Factor Analysis and Countermeasures of Porosity and Pipe in Ingot;

钢锭疏松、缩孔的因素分析及对策

In this paper, analysis on the fissuring accident of ZGMn13Cr2Mo antifriction tup is performed, and the reason is believed to lie in serious casting defects of shrinkage cavity, porosity and inclusion.

对ZGMn13Cr2Mo耐磨锤头的断裂事故进行了分析,主要原因是存在着严重的铸造缺陷:缩孔、疏松和夹杂物。

5) Looseness

疏松

Results indicate that the primary cause to the rupture of the screw in the process of torque force test is proved to be heavily existence of holes and pore gaps in the screw arising from the central looseness of the original billet.

结果得出:螺钉在扭力试验过程中断裂是由于内部存在严重的孔洞和孔隙所造成的,孔洞和孔隙来源于原铸坯的中心疏松。

Mechanism of central parosity and looseness of small billet is described and analysed.

简述小方坯中心缩孔和疏松的形成机理 ,提出减轻中心缩孔和疏松的措

The experimental results show that there are some internal metallurgy flaws such as looseness,shrink hole in the raw material of the axle,and bad widmanstatten structure from the overheating and over-burning during the heating of forging,the comprehensive effects of these factors cause the steel toughness to reduce,and the internal cleavage exists d.

结果表明,车轴轴头原材料中存在疏松、缩孔残余等内部冶金缺陷和锻造热加工中的过热和过烧产生不良的魏氏组织,这些因素的综合作用致使钢的韧性降低,在锻造中发生内部劈裂,最终造成轴头在受外力时脆性断裂。

6) porous

疏松

A new heterogeneous polymerization process, in which water acted as a dispersed phase and methyl methacrylate (MMA) as a continuous phase, was developed to prepare porous poly(methyl methacrylate) (PMMA) resin.

　以水为分散相、甲基丙烯酸甲酯(MMA)为连续相进行悬浮态乳液聚合,合成疏松型聚甲基丙烯酸甲酯(PMMA)树脂。

7) shrinkage porosity

疏松

Mold-filling, solidification and prediction of shrinkage porosity in Ti-46%Al alloy investment were performed using the ViewCast code, and the defects observed in the actual products agree well with the simulated results.

应用铸造软件ViewCast模拟精密铸造Ti 46%Al合金叶片的充型与凝固过程,预测了疏松的形成,模拟结果与实验结果相吻合。

8) loose

疏松

Vibroflotation compaction is a comparably mature method for the improvement of cohesiveless soils,but it is seldom used to strengthen loose silty fine sands,especially for depth over 15m.

结合上海市某重点工程,基于吹填粉细砂的工程特性,通过现场试验探索出振冲工艺的主要设计和施工参数,对深度15m以上的饱和疏松粉细砂地基采用振冲加固的有效性进行了现场试验研究。

They are as following: there is loose defect on the inner side,at the same time ther.

本文对开裂的阀体取样进行了化学成分、力学性能和金相组织的测定,找出了造成ZG20CrMoV阀体打水压断裂的主要原因是内部有疏松缺陷,内表面有沿着疏松长十几毫米的裂纹,再加上塑性和韧性都低,造成了最终打水压时的开裂。

9) osteoporosis

骨质疏松

Experimental Study of The Effect of OPGmRNA and RANKLmRNA about The method of Bu Shen Jian Pi on The Osteoporosis rat;

补肾健脾法对骨质疏松大鼠OPGmRNA、RANKLmRNA表达影响的实验研究

Effects of Bushenfugai Traditional Chinese Medicine on morphometry of osteoporosis induced by ovary irradiation in rats;

补肾富钙中药对大鼠卵巢辐射损伤所致骨质疏松形态计量学的影响

Progress in the research into the relationshipbetween osteoporosis and jaw implant;

骨质疏松症与颌骨种植体关系研究进展

10) internal defect

内部疏松

Theorectical and experimental study on internal defect of equal diameter axis formed in multi-wedge cross wedge rolling;

楔横轧多楔成形等直径轴类件内部疏松的理论与实验研究

补充资料：疏松

疏松
poriness

　　shusong疏松(poriness)钢材的内部缺陷之一，表现为金属横断面酸浸低倍试样上呈现组织不致密，有许多分散的孔隙和小黑点，树枝状结晶粗大，主干和各枝间致密度差别分明，孔隙呈不规则多边形，严重时呈海绵状(见图).在整个试片上表现出组织不致密的叫一般疏松。在中心处集中许多孔隙和黑点时叫中心疏松，纵向酸浸试片上疏松表现为不同长度的条纹，但深度很浅，同裂纹有本质区别。疏松根据产品标准的有关评鬃疏松级图片鉴定。疏松是金属液凝固时体积收缩引起的小孔隙、树枝状结晶的枝间孔隙及低熔点物质最后凝固放出的气体所形成的微孔的聚集，微孔中及附近有一些夹杂物。含碳量高的钢出现得多。采用充分脱氧、去气和浇铸时及时充填液体金属控制浇铸温度及速度可减少疏松。热加工锻轧可傅疏松焊合，提高金属的致密度。 (崔峰许庆泰)
　　

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

疏松剂疏松油藏疏松区疏松材料疏松砂体一般疏松疏松点疏松孔洞疏松介质疏松物紫珠属植物复烘[热固性塑料]

中心疏松疏松砂岩疏松地层显微疏松疏松底材心部疏松
1) loose structure 疏松结构 2) gassy surface 疏松结构 3) fuzzy texture 疏松结构(搪瓷) 4) porosity 疏松 1. Effect of electric current pulse on shrinkage cavity and porosity in casting ZA27 alloy; 脉冲电流对铸造ZA27合金中缩孔和疏松的影响 2. Factor Analysis and Countermeasures of Porosity and Pipe in Ingot; 钢锭疏松、缩孔的因素分析及对策 3. In this paper, analysis on the fissuring accident of ZGMn13Cr2Mo antifriction tup is performed, and the reason is believed to lie in serious casting defects of shrinkage cavity, porosity and inclusion. 对ZGMn13Cr2Mo耐磨锤头的断裂事故进行了分析,主要原因是存在着严重的铸造缺陷:缩孔、疏松和夹杂物。 5) Looseness 疏松 1. Results indicate that the primary cause to the rupture of the screw in the process of torque force test is proved to be heavily existence of holes and pore gaps in the screw arising from the central looseness of the original billet. 结果得出:螺钉在扭力试验过程中断裂是由于内部存在严重的孔洞和孔隙所造成的,孔洞和孔隙来源于原铸坯的中心疏松。 2. Mechanism of central parosity and looseness of small billet is described and analysed. 简述小方坯中心缩孔和疏松的形成机理 ,提出减轻中心缩孔和疏松的措 3. The experimental results show that there are some internal metallurgy flaws such as looseness,shrink hole in the raw material of the axle,and bad widmanstatten structure from the overheating and over-burning during the heating of forging,the comprehensive effects of these factors cause the steel toughness to reduce,and the internal cleavage exists d. 结果表明,车轴轴头原材料中存在疏松、缩孔残余等内部冶金缺陷和锻造热加工中的过热和过烧产生不良的魏氏组织,这些因素的综合作用致使钢的韧性降低,在锻造中发生内部劈裂,最终造成轴头在受外力时脆性断裂。 6) porous 疏松 1. A new heterogeneous polymerization process, in which water acted as a dispersed phase and methyl methacrylate (MMA) as a continuous phase, was developed to prepare porous poly(methyl methacrylate) (PMMA) resin. 　以水为分散相、甲基丙烯酸甲酯(MMA)为连续相进行悬浮态乳液聚合,合成疏松型聚甲基丙烯酸甲酯(PMMA)树脂。 7) shrinkage porosity 疏松 1. Mold-filling, solidification and prediction of shrinkage porosity in Ti-46%Al alloy investment were performed using the ViewCast code, and the defects observed in the actual products agree well with the simulated results. 应用铸造软件ViewCast模拟精密铸造Ti 46%Al合金叶片的充型与凝固过程,预测了疏松的形成,模拟结果与实验结果相吻合。 8) loose 疏松 1. Vibroflotation compaction is a comparably mature method for the improvement of cohesiveless soils,but it is seldom used to strengthen loose silty fine sands,especially for depth over 15m. 结合上海市某重点工程,基于吹填粉细砂的工程特性,通过现场试验探索出振冲工艺的主要设计和施工参数,对深度15m以上的饱和疏松粉细砂地基采用振冲加固的有效性进行了现场试验研究。 2. They are as following: there is loose defect on the inner side,at the same time ther. 本文对开裂的阀体取样进行了化学成分、力学性能和金相组织的测定,找出了造成ZG20CrMoV阀体打水压断裂的主要原因是内部有疏松缺陷,内表面有沿着疏松长十几毫米的裂纹,再加上塑性和韧性都低,造成了最终打水压时的开裂。 9) osteoporosis 骨质疏松 1. Experimental Study of The Effect of OPGmRNA and RANKLmRNA about The method of Bu Shen Jian Pi on The Osteoporosis rat; 补肾健脾法对骨质疏松大鼠OPGmRNA、RANKLmRNA表达影响的实验研究 2. Effects of Bushenfugai Traditional Chinese Medicine on morphometry of osteoporosis induced by ovary irradiation in rats; 补肾富钙中药对大鼠卵巢辐射损伤所致骨质疏松形态计量学的影响 3. Progress in the research into the relationshipbetween osteoporosis and jaw implant; 骨质疏松症与颌骨种植体关系研究进展 10) internal defect 内部疏松 1. Theorectical and experimental study on internal defect of equal diameter axis formed in multi-wedge cross wedge rolling; 楔横轧多楔成形等直径轴类件内部疏松的理论与实验研究补充资料：疏松疏松 poriness 　　shusong疏松(poriness)钢材的内部缺陷之一，表现为金属横断面酸浸低倍试样上呈现组织不致密，有许多分散的孔隙和小黑点，树枝状结晶粗大，主干和各枝间致密度差别分明，孔隙呈不规则多边形，严重时呈海绵状(见图).在整个试片上表现出组织不致密的叫一般疏松。在中心处集中许多孔隙和黑点时叫中心疏松，纵向酸浸试片上疏松表现为不同长度的条纹，但深度很浅，同裂纹有本质区别。疏松根据产品标准的有关评鬃疏松级图片鉴定。疏松是金属液凝固时体积收缩引起的小孔隙、树枝状结晶的枝间孔隙及低熔点物质最后凝固放出的气体所形成的微孔的聚集，微孔中及附近有一些夹杂物。含碳量高的钢出现得多。采用充分脱氧、去气和浇铸时及时充填液体金属控制浇铸温度及速度可减少疏松。热加工锻轧可傅疏松焊合，提高金属的致密度。 (崔峰许庆泰) 　　说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条疏松剂疏松油藏疏松区疏松材料疏松砂体一般疏松疏松点疏松孔洞疏松介质疏松物紫珠属植物复烘[热固性塑料]
©2008 dictall.com