1) parylene
['pɑ:rili:n]
聚对二甲苯基
2) poly-p-xylyiene
聚对二亚甲基苯
3) poly(p-xylylene)
聚对亚苯基二亚甲基
1.
Sulfonated modification of poly(p-xylylene) prepared by CVDP;
CVDP制备的聚对亚苯基二亚甲基的表面磺化改性
2.
In the present work poly(p-xylylene)(PPX) is prepared by chemical vapor deposition(CVD) polymerization from paracyclophane.
用化学气相沉积(CVD)聚合法制备了聚对亚苯基二亚甲基(PPX)膜,由傅立叶变换红外光谱(FTIR)图证实了其化学结构。
3.
Poly(p-xylylene)(PPX) membranes were prepared by chemical vapor deposition polymerization.
采用化学气相沉积聚合(CVDP)法制备聚对亚苯基二亚甲基(PPX),再通过与酸酐的化学表面反应将丁酸酰基和马来酰基引入PPX薄膜的表面,制得表面带活性取代基的PPX。
4) poly(acetyl p-xylylene)
聚乙酰基对苯撑二甲基
1.
In this paper poly(acetyl p-xylylene) was prepared by chemical vapor deposition (CVD) polymerization.
通过化学气相沉积(CVD)聚合法合成了聚乙酰基对苯撑二甲基,采用红外光谱(FTIR)证实了二聚体和气相沉积聚合物的化学结构。
5) parylene
['pɑ:rili:n]
聚对二甲苯
1.
Fabrication of the parylene film by the method of hot-wire assistance;
热丝辅助裂解法制备聚对二甲苯薄膜
2.
By dip-coating process,parylene film could be associated with SiO_2 AR-coating to act as protective film of KDP crystal.
报道了采用真空化学气相沉积法制备的聚对二甲苯薄膜和采用溶胶-凝胶技术制备的二氧化硅增透膜,通过提拉镀膜法在聚对二甲苯薄膜表面镀制 SiO_2增透膜得到的双层膜可应用于 KDP 晶体的增透保护膜。
3.
The paper focuses on vacuum vapor deposition for making parylene film which is used in many targets.
介绍了真空气相沉积法制备聚对二甲苯薄膜的实验设备、实验原理和实验方法。
6) Poly(p-xylylene)
聚对二甲苯
1.
Study on preparation and optical properties of Poly(p-xylylene)/SiO_2 composite film;
聚对二甲苯/SiO_2复合薄膜的制备及光学性能研究
2.
The preparation methods, mechanism of forming film, film properties and application fields of poly(p-xylylene) are reviewed.
聚对二甲苯是一种性能优异的涂层材料。
补充资料：聚对二甲苯
分子式：
CAS号：
性质： 主链由亚乙基和亚苯基交替排列构成的一类聚合物。由对二甲苯经真空蒸发沉积工艺聚合而成。密度1.11g/cm3，熔点达400℃。热氧稳定性较差，在惰性气体中可于220℃连续使用，空气中仅在90～130℃连续使用。电气性能十分优良，150℃以下耐任何有机溶剂。主要用作电容器、电子零件和电子线路板的绝缘介质和涂层。
CAS号：
性质： 主链由亚乙基和亚苯基交替排列构成的一类聚合物。由对二甲苯经真空蒸发沉积工艺聚合而成。密度1.11g/cm3，熔点达400℃。热氧稳定性较差，在惰性气体中可于220℃连续使用，空气中仅在90～130℃连续使用。电气性能十分优良，150℃以下耐任何有机溶剂。主要用作电容器、电子零件和电子线路板的绝缘介质和涂层。