1) microdilatometer
微膨胀计
2) micro-expansion
微膨胀
1.
Method The effect of developing low heating temperature and micro-expansion of fast strength slag Portland cement was affected by the slag activity,fineness,dosage and phosphogypsum component.
方法研究矿渣的活性、细度、掺量及磷石膏对生产低热微膨胀早强矿渣水泥性能的影响,并试验研究该水泥的其它性能。
2.
The joints cement has the performance of micro-expansion.
通过特别工艺,研制出C aO为主要成分的膨胀剂,用于浇筑水泥时其掺入量以3%为宜,研制的浇筑水泥,具有微膨胀性能。
3.
The LE-PG early high strength micro-expansive grouting material is of early high strength,micro-expansion,self-leveling,self-thickness,anti-oil immersion,resistance to long-term application,strong availability and convenience for construction,etc.
JE -PG早高强微膨胀灌浆料具有早高强、微膨胀、自流平、自密实、抗油浸、耐长久、适用性强、施工方便等优良性能。
3) slight expansibility
微膨胀性
4) slight expanded-bed
微膨胀床
1.
Research on slight expanded-bed oil residue hydrotreating reactor;
微膨胀床渣油加氢处理反应器的研究
5) slight expansion
微膨胀
1.
Construction test of slight expansion(SE) concrete made from moderate heat Portland cement with double expansive sources(DE cement) and 20% fly ash was carried out and analysed with instruments buried in mass concrete in Lingjintan dam for measuring concrete deformation.
通过在大体积混凝土浇块中埋设水工观测仪器的方法,对由双膨胀中热水泥和粉煤灰拌制的微膨胀混凝土(C15)进行了现场观测和分析。
2.
In the effects of superplasticizer, a high-performance cement-based grouting material with an early strength, high strength, high fluidity, no bleeding, slight expansion was successfully developed at a low water-cement ratio and various components’influ
通过在水泥中掺加硅灰、石英粉、膨胀剂和纳米SiO2,用比水泥颗粒尺寸小1～2个数量级的硅灰填充水泥颗粒之间的空隙,减少水泥颗粒之间的空隙率,增加水泥石的密实程度,再用颗粒尺寸更小的纳米级SiO2填充水泥与硅灰之间的空隙,使得整个胶凝体系的密实度达到最大,系统的需水量也降到最低,在高效减水剂的作用下,制得在很低的水胶比条件下具有早强、高强、高流动性、无泌水、微膨胀的高性能水泥基灌浆材料,并分析各种组成成分对DSP灌浆材料各项性能的影响,论文的主要研究内容和成果如下:(1)研究了硅灰水泥质量比对灌浆材料强度和流动性能的影响,试验得出灌浆材料的强度和流动性同时达到最佳状态时的最佳硅灰水泥质量比。
3.
Through a large number of experiments,a high-performance cement-based grouting material with a 1d compressive strength≥45 MPa,28d compressive strength≥110 MPa spread≥400 mm,no bleeding,slight expansion,early-strength and high-strength was successfully achieved.
通过大量的实验,研制出1 d强度高达45 MPa,28 d强度高达110 MPa,扩展度超过400mm,无泌水,微膨胀的早强、高强的高性能水泥基灌浆材料。
6) micro expansive
微膨胀
1.
The mix proportion design of micro expansive and self dense of C50 pump concrete;
C50微膨胀自密实泵送混凝土配合比设计
补充资料：低热微膨胀水泥
分子式：
分子量：
CAS号：
性质：以粒化高炉矿渣为主要组分，加入适量硅酸盐水泥熟料和石膏，磨细制成的具有低水化热和微膨胀性能的水硬性胶凝材料。该水泥按强度等级分为325、425两个标号。主要适用于要求较低水化热和要求补偿收缩的混凝土、大体积混凝土，也适用于要求抗渗和抗硫酸盐侵蚀的工程。
分子量：
CAS号：
性质：以粒化高炉矿渣为主要组分，加入适量硅酸盐水泥熟料和石膏，磨细制成的具有低水化热和微膨胀性能的水硬性胶凝材料。该水泥按强度等级分为325、425两个标号。主要适用于要求较低水化热和要求补偿收缩的混凝土、大体积混凝土，也适用于要求抗渗和抗硫酸盐侵蚀的工程。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。