1) low-solubility glaze
低铅溶出釉
2) lead release
铅溶出量
1.
This article is to analyse how the acid effect and precipitation effect of the medium influence the measurement of the lead release of daily-use ceramics in 4PCT (V/V) leach liquor of formic acid which contains different media.
分析了含有不同介质的4％(V／V)乙酸浸提液中,介质的酸效应、沉淀效应对日用陶瓷铅溶出量测定的影响,指出沉淀效应是影响陶瓷铅溶出量的主要因素。
2.
The factors influencing lead release of the porcelain products were discussed,the ways and the methods decreasing lead release of the porcelain products were explored.
主要论述了影响彩饰陶瓷制品铅溶出量的因素，并对降低陶瓷制品铅溶出量的途径及措施进行了探讨。
3) lead dissolution
铅溶出
4) lead and cadmium dissolve
铅镉溶出
1.
The influence factors of lead and cadmium dissolve were discussed and then put forward some solve measures.
介绍了釉上彩、釉中彩、釉下彩三种装饰方法及其优缺点,论述了影响陶瓷花纸装饰铅镉溶出的因素,并给出了解决措施。
5) low-temperature and lead-free fritted glaze
低温无铅熔块釉
6) Lead-free&cadmium-free release
无铅镉溶出
补充资料：固溶量
分子式：
CAS号：
性质： 有限固溶体中某组分的溶解度。通常利用X射线衍射仪测定晶胞常数的变化及是否出现第2晶相来研究溶解的极限量。固溶量大小与两物质的离子半径大小、价数、配位数及温度等因素有关例如，CaO和MgO都是NaCl型立方晶体，在高温下可以相互固溶成两种有限固溶体，当MgO溶入CaO晶格中因Mg2+离子半径较小，因此随MgO溶入量增加CaO固溶体晶胞不断变小，到极限溶解量后，晶格就不再变化，从而测得MgO在CaO中的固溶量约为17％。进一步添加MgO，将出现CaO固溶体和MgO的X射线衍射的特征线条。
CAS号：
性质： 有限固溶体中某组分的溶解度。通常利用X射线衍射仪测定晶胞常数的变化及是否出现第2晶相来研究溶解的极限量。固溶量大小与两物质的离子半径大小、价数、配位数及温度等因素有关例如，CaO和MgO都是NaCl型立方晶体，在高温下可以相互固溶成两种有限固溶体，当MgO溶入CaO晶格中因Mg2+离子半径较小，因此随MgO溶入量增加CaO固溶体晶胞不断变小，到极限溶解量后，晶格就不再变化，从而测得MgO在CaO中的固溶量约为17％。进一步添加MgO，将出现CaO固溶体和MgO的X射线衍射的特征线条。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条