1) imitation glassine paper
仿玻璃纸
3) Jade-like glass
仿玉玻璃
1.
Jade-like glass with soft color and Luster can be obtained by adding an appropriate amount of emulsion agent (Na2SiF6) in the basic glass.
在基础玻璃中加入适量的乳浊剂(Na2SiF6)可以制得光色柔润的仿玉玻璃,基础玻璃的组成、乳浊剂(Na2SiF6)的引入量、Al2O3的引入量对仿玉玻璃的光色性能有重要影响,熔制温度的高低、熔制时间的长短以及生产工艺过程的稳定等都会影响仿玉玻璃的光色性能。
4) cellophane
[英]['seləfeɪn] [美]['sɛlə'fen]
玻璃纸
1.
The generation principles of the waste gas containing CS2 and H2S in the manufatcture of cellophane and the current situation of its treatment are introduced.
阐述了玻璃纸生产中CS2和H2S废气产生的原理,介绍了该废气处理的现状,总结了目前普遍采用的冷凝法、活性炭吸附法、活性碳纤维吸附法、改性活性炭吸附法、螯合铁氧化法、吸收—吸附法等处理方法的特点和效果。
2.
Fragility causes of cellophane are discussed and corresponding solutions are brought forward.
探讨了生产过程中引起玻璃纸发脆的原因并提出了相应的解决办
3.
The cellophane and visking dialysis tubing were used in the experiment for dialyzing the Ca2+ from fibroin solution.
用透析袋和玻璃纸为透析材料，分别透析去除丝素溶液中Ｃａ２＋，并就透析后丝素溶液中的Ｃａ２＋含量和含氮量进行了分析对比。
5) cast coating cardboard
玻璃卡纸
6) glass paper
玻璃砂纸
补充资料：玻璃纸
分子式：
CAS号：
性质：又称赛璐玢。一种透明度高并有光泽的再生纤维素薄膜。有平板纸和卷筒纸。定量30～60g/m2。无色，也可染成各种颜色。纸质柔软、透明光滑，无孔眼，不透气，不透油，不透水。有适度的挺度。具有较好的拉伸强度、光泽性和印刷适性。生产方法与造纸不同，与人造丝工艺相近。采用α-纤维素含量高的精制化学木浆或棉短绒溶解浆为原料，经碱化(18％氢氧化钠)、压榨、粉碎等过程制得碱纤维素，再经老化后加入二硫化碳使之黄化成纤维素黄原酸酯，用氢氧化钠溶液溶解即制成橘黄色的纤维素黏胶。该黏胶在20～30℃温度下进行熟成处理，并经过滤除去杂质和脱除气泡，然后在拉膜机中由一个狭长的缝隙中挤出，流入硫酸和硫酸钠混合液的凝固浴槽中，形成薄膜(再生纤维素薄膜)，再经水洗、脱硫、漂白、脱盐和塑化(甘油和乙二醇等)等处理，最后经干燥制成。用于药品、食品、香烟、纺织品、化妆品、精密仪器等商品的包装。
CAS号：
性质：又称赛璐玢。一种透明度高并有光泽的再生纤维素薄膜。有平板纸和卷筒纸。定量30～60g/m2。无色，也可染成各种颜色。纸质柔软、透明光滑，无孔眼，不透气，不透油，不透水。有适度的挺度。具有较好的拉伸强度、光泽性和印刷适性。生产方法与造纸不同，与人造丝工艺相近。采用α-纤维素含量高的精制化学木浆或棉短绒溶解浆为原料，经碱化(18％氢氧化钠)、压榨、粉碎等过程制得碱纤维素，再经老化后加入二硫化碳使之黄化成纤维素黄原酸酯，用氢氧化钠溶液溶解即制成橘黄色的纤维素黏胶。该黏胶在20～30℃温度下进行熟成处理，并经过滤除去杂质和脱除气泡，然后在拉膜机中由一个狭长的缝隙中挤出，流入硫酸和硫酸钠混合液的凝固浴槽中，形成薄膜(再生纤维素薄膜)，再经水洗、脱硫、漂白、脱盐和塑化(甘油和乙二醇等)等处理，最后经干燥制成。用于药品、食品、香烟、纺织品、化妆品、精密仪器等商品的包装。