1) furfuryl resin
糠基树脂
2) Furfuralcohol resin
糠醇树脂
1.
The results found that the resin carbon materials treated at 620℃ have evidently appeared (100) crystal plane diffraction peek,at one time the (110) and (006) crystal plane diffraction peeks also appeared,it means that the furfuralcohol resin is a type of facility graphitization resin material.
测试分析了碳化处理条件对糠醇树脂碳化产物组成、结构和电化学性能的影响。
2.
Furfuralcohol resin was carbonized to make carbon materials.
测试分析了炭化处理条件对糠醇树脂炭化产物组成和结构的影响。
3) furfural resin
糠醇树脂
1.
Mechanism and application of furfural resin sand consolidation agent modified by organic silicone;
硅氧烷糠醇树脂固砂剂的作用机理及应用
2.
The graphite degrees and structure parameters of resin carbons derived from furfural resin and polyaniline resin were investigated by X-ray diffraction method.
采用X光衍射法对糠醇树脂和聚苯胺树脂碳化产物的石墨化度和微观结构进行了研究。
4) furfural acetone resin
糠酮树脂
1.
Curing reaction of furfural acetone resin used for new carbon materials;
新型炭材料用糠酮树脂的固化特性
2.
Using furfural and acetone as the raw material,we gained furfural acetone resin by condensation and distillation through ion exchange resin catalysis process along with the mineral acid alkali catalysis process.
以糠醛和丙酮为原料,采用阴阳离子交换树脂二步催化法合成工艺,通过缩合、过滤、缩聚、蒸馏制得糠酮树脂产品。
5) furfuryl alcohol modified urea formaldehyde resin
糠脲树脂
补充资料：糠醇树脂
分子式：
CAS号：
性质：糠醇的缩聚物。红色黏稠不易流动的液体，能溶于丙酮、醇、醚类等，不溶于苯。以无机酸或有机酸作固化剂。强酸(如硫酸或对甲苯磺酸)可使树脂室温固化。弱酸(如苯二甲酸酐、顺丁烯二酸酐、磷酸)需在95～200℃下数小时后方能使树脂固化，故适于低压成型。固化物耐酸(不耐强氧化性酸)，耐碱，耐有机溶剂，耐水，耐热性较好，硬度较高，与碳、石墨、石棉、玻纤有较好的粘接性。缺点是脆性大，对非多孔性物质表面的附着力差，固化收缩率大。树脂由糠醇在酸性催化剂作用下缩聚而成。主要用于耐腐蚀涂料、衬里、胶泥、玻璃钢管道、阀门、泵体及模压制品和木材、铸造用黏合剂。
CAS号：
性质：糠醇的缩聚物。红色黏稠不易流动的液体，能溶于丙酮、醇、醚类等，不溶于苯。以无机酸或有机酸作固化剂。强酸(如硫酸或对甲苯磺酸)可使树脂室温固化。弱酸(如苯二甲酸酐、顺丁烯二酸酐、磷酸)需在95～200℃下数小时后方能使树脂固化，故适于低压成型。固化物耐酸(不耐强氧化性酸)，耐碱，耐有机溶剂，耐水，耐热性较好，硬度较高，与碳、石墨、石棉、玻纤有较好的粘接性。缺点是脆性大，对非多孔性物质表面的附着力差，固化收缩率大。树脂由糠醇在酸性催化剂作用下缩聚而成。主要用于耐腐蚀涂料、衬里、胶泥、玻璃钢管道、阀门、泵体及模压制品和木材、铸造用黏合剂。