1) cast nickle alloy tooth
镍基铸造合金牙
2) Cast Iron-Nickel-Base Alloy
铸造铁镍基合金
3) Ni-base alloy for casting
铸造镍基合金
1.
The influence of rare earth modification on the improvement of structure and corrosion resistance of Ni-base alloy for casting as well as on its casting properties is studied in this, paper.
本文研究了稀土变质处理对改善铸造镍基合金的组织和耐蚀性能与铸造性能的影响。
5) cast Ni-base superalloy
铸造镍基高温合金
1.
The oxidation behavior of a cast Ni-base superalloy K447 in air ina temperature range of 700 to 950℃ for period up 100h has been studied.
用静态增重法测定了铸造镍基高温合金K447在700℃~950℃空气中的恒温氧化行为,其氧化动力学符合抛物线规律。
2.
The oxidation behavior of a cast Ni-base superalloy K35 in air over the temperature range of 850 to 1000℃ for period up to 100 h has been studied.
测定了铸造镍基高温合金K35在850—1000℃温度范围内的氧化动力学曲线;并计算出其氧化激活能Q_(p1)=274 kJ/mol,Q_(p2)=315 kJ/mol,其氧化动力学曲线都符合抛物线规律,900℃以下,K35合金属于完全抗氧化级;900—1000℃为抗氧化级,X射线衍射、扫描电镜和能谱分析表明,K35合金的氧化膜分为3个区域:外层是性质疏松的Ti及Cr氧化物混合层,并含有少量尖晶石NiCr_2O_4与NiAl_2O_4;中间层是性质致密的Cr_2O_3氧化层;内层(过渡层)是Al_2O_3。
6) Cast Ni-base superalloy K52
K52镍基铸造高温合金
补充资料：铁基铸造高温合金
分子式：
CAS号：
性质：在600～950℃使用的铁基铸造奥氏体高温合金。通常含有10％～45％Ni以稳定奥氏体基体。分为两种类型：一类是碳化物强化的铁基铸造高温合金；另一类是金属间化合物强化的铁基铸造高温合金。与镍基铸造高温合金相比，其价格便宜，但组织稳定性较差，金属间化合物强化效果在700℃左右开始失效，高温强度明显不及镍基铸造高温合金，在中温以下，强度又不及变形铁基和镍基高温合金，故应用范围远不如变形铁基高温合金。但在制作承力较小的部件上具有成本低的优点，广泛应用于石油和化工的裂化与催化管材、发动机机匣与喷嘴等方面。
CAS号：
性质：在600～950℃使用的铁基铸造奥氏体高温合金。通常含有10％～45％Ni以稳定奥氏体基体。分为两种类型：一类是碳化物强化的铁基铸造高温合金；另一类是金属间化合物强化的铁基铸造高温合金。与镍基铸造高温合金相比，其价格便宜，但组织稳定性较差，金属间化合物强化效果在700℃左右开始失效，高温强度明显不及镍基铸造高温合金，在中温以下，强度又不及变形铁基和镍基高温合金，故应用范围远不如变形铁基高温合金。但在制作承力较小的部件上具有成本低的优点，广泛应用于石油和化工的裂化与催化管材、发动机机匣与喷嘴等方面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。