1) torsional cracking
扭转开裂
2) Torsion stiffness of R. C. beam after cracking
开裂扭转刚度
3) cracking torque
开裂扭矩
1.
It is shown that the axial stress level and relative eccentricity have greatly effect on the angle of cracks and cracking torque of members.
以轴压比和相对偏心距为参数,对8根高强钢筋混凝土压弯剪构件在单调扭矩作用下的性能进行了试验研究,探讨了试件裂缝的产生和发展、破坏特征以及影响裂缝倾角和开裂扭矩的因素。
2.
An equation for calculating the cracking torque of r ei nforced concrete members subjected to combined torsion is derived.
推导了钢筋混凝土复合受扭构件开裂扭矩计算公式 ,分析了弯矩、压力、剪力对开裂扭矩的影响 。
3.
The limitation and theoretic one - sidedness of the present formula in calculation efficiency of the prestressing force to affect the cracking torque are pointal out.
指出了现有的开裂扭矩预应力影响系数计算公式的局限性及其理论上的片面性。
4) cracking due to torsion and shear
扭剪开裂
5) torsional fissure
扭转裂缝
6) torsional fracture
扭转断裂
1.
The results show that the fracture was caused by the banded structure which decreased the permitted rotational moment and resulted in the torsional fracture of the bolts during installation process.
结果表明:螺栓断裂是由于其制造时产生了严重的带状组织,降低了螺栓的许可扭转力矩,导致螺栓在安装过程中发生扭转断裂。
补充资料：穿晶开裂
分子式：
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。