1) cracking moment
开裂力矩
2) cracking torque
开裂扭矩
1.
It is shown that the axial stress level and relative eccentricity have greatly effect on the angle of cracks and cracking torque of members.
以轴压比和相对偏心距为参数,对8根高强钢筋混凝土压弯剪构件在单调扭矩作用下的性能进行了试验研究,探讨了试件裂缝的产生和发展、破坏特征以及影响裂缝倾角和开裂扭矩的因素。
2.
An equation for calculating the cracking torque of r ei nforced concrete members subjected to combined torsion is derived.
推导了钢筋混凝土复合受扭构件开裂扭矩计算公式 ,分析了弯矩、压力、剪力对开裂扭矩的影响 。
3.
The limitation and theoretic one - sidedness of the present formula in calculation efficiency of the prestressing force to affect the cracking torque are pointal out.
指出了现有的开裂扭矩预应力影响系数计算公式的局限性及其理论上的片面性。
3) crack moment
开裂弯矩
1.
In order to restrict the bound of formula, the formula of crack moment is obtained.
同时推导出了开裂弯矩的计算公式,确定了滑移和变形挠度计算公式的适用范围。
4) cracking moment
开裂弯矩
1.
On the calculation of reinforced concrete beam and pile cracking moment and yield moment;
钢筋混凝土梁和柱开裂弯矩及屈服弯矩的计算
2.
With the basic formula of rectangular section concrete member with compression and flexure, the calculation formula of cracking moment of concrete compressive and flexural member was derived.
根据钢筋混凝土矩形截面压弯构件的基本方程,导出了压弯构件的开裂弯矩表达式,通过计算,给出了开裂弯矩与混凝土强度等级、轴压比和配筋率之间的变化规律,从而得出了具有配筋率和轴压比参数的开裂弯矩计算公式,该公式形式简单,与试验结果符合较好。
3.
The experimental results of 16 haydite concrete one-way slabs show that the cracking moment,ultimate moment,crack width and deflection under service load conditions of the tested slabs meet the requirement of technical specification for lightweight aggregate concrete.
对16块陶粒混凝土单向板进行试验研究,板的开裂弯矩、极限弯矩、正常使用条件下的裂缝宽度和挠度符合国家行业标准的技术要求。
5) crack-resistant moment
开裂弯矩
1.
Based upon the tests on 12 steel fiber reinforced high-strength concrete beams with reinforcements,the effect of steel fiber on the normal cross sectional crack-resistant moment of steel fiber reinforced high-strength concrete beams is analysed.
实验结果表明,钢纤维的加入提高了钢筋高强混凝土梁的正截面开裂弯矩,并随着钢纤维体积率的增加呈增长的趋势,增加幅度在40%~100%之间;纵向钢筋配筋率、梁的高度以及钢筋的强度等级对钢筋高强混凝土梁的开裂弯矩也有影响;开裂弯矩随纵筋配筋率的增大以及随截面高度的减小而增大。
6) moment of rupture
断裂力矩
补充资料：扭矩传感器
分子式：
CAS号：
性质：能使物体产生某种程度的扭转变形的力偶或力矩称为扭转力矩，简称扭矩。扭矩测量是各种机械产品的测试分析、质量检验中的重要参数；另外，为了及时监测运动中的设备的负荷大小和运行状况，则要对扭矩进行在线检测。扭矩传感器有磁弹性扭矩传感器、电阻应变片式扭矩传感器、和磁电式、光电式相位差扭矩传感器等。
CAS号：
性质：能使物体产生某种程度的扭转变形的力偶或力矩称为扭转力矩，简称扭矩。扭矩测量是各种机械产品的测试分析、质量检验中的重要参数；另外，为了及时监测运动中的设备的负荷大小和运行状况，则要对扭矩进行在线检测。扭矩传感器有磁弹性扭矩传感器、电阻应变片式扭矩传感器、和磁电式、光电式相位差扭矩传感器等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条