1) hot hardening
加热硬化
2) hot work hardening
热加工硬化
4) Work hardening
加工硬化
1.
Investigation of work hardening mechanism in high manganese steel by Crussard-Jaoul analysis;
基于Crussard-Jaoul的n值分析对高锰钢加工硬化机制的探讨
2.
The simulation results suggest that Bauschinger effect and work hardening etc are validated in the model.
模拟结果表明,弯曲过程中存在鲍辛格效应和加工硬化等现象。
3.
The results show that the effects of work hardening by strain-induced martensite transformation and cast pore defects are the main reasons leading to strip broken of the steels during cold rolling.
结果表明,形变诱发马氏体组织所加剧的加工硬化与冶炼时所产生的气孔缺陷的共同作用是冷轧断带的原因。
5) work-hardening
加工硬化
1.
The results indicate that the developed surfacing electrode has not only good welding technological properties,but also super work-hardening effect and good impact wear-resistance.
经过对制备的试样分别进行多次冲击磨损试验,并与D256焊条进行对比试验,分析试样的硬度和磨损失重变化,结果表明,此种堆焊材料具有焊接工艺性好、堆焊层组织加工硬化率高和耐凿削式冲击磨损性能优异的特点。
2.
the tensile strength and rate of elogation were measured by tension experiment machine,the situation of work-hardening was analysed,and the rolling direction cross-section metallurgical structure of the sheets under different deformation was analysed.
在二辊轧机上对CSP轧制的SPHD钢板进行了冷变形,在拉伸试验机上测定了冷变形后钢板的抗拉强度和伸长率,分析了其加工硬化的情况,并对不同冷变形程度下钢板轧制方向的横截面组织进行了分析。
3.
The important character of non-magnetic high manganese ZG25Mn18Cr4 alloy is rapid work-hardening under external stress.
在应力作用下快速加工硬化是高锰无磁钢ZG25Mn18Cr4的一个重要特征。
6) strain hardening
加工硬化
1.
The results show that the grain size of the deep deformed Hadfield steel was refined remarkably,there emerge a great deal of high density twin crystals and stacking faults,and the capability of strain hardening and wear resistance are enhanced greatly.
试验结果表明,经预变形的高锰钢奥氏体晶粒急剧细化,内部出现大量的高密度孪晶、位错缠结及层错等组织,加工硬化性能大大提高,耐磨性也随之提高。
2.
Its strain hardening exponent n is 0.
挤压态合金的加工硬化指数n为0。
3.
The strain hardening rate of the material in various aging states is also increased by this addition, wh.
强化颗粒的加入还显著提高了材料在各种时效状态的加工硬化率。
补充资料：工程塑料硬度的检测--巴氏硬度计
HBa-1巴 氏 硬 度 计巴柯尔 (Barcol) 硬度 ( 简称巴氏硬度 ) 最早由美国 Barber-Colman 公司提出，是近代国际上广泛采用的一种硬度门 类，以特定压头在标准弹簧的压力作用下压入试样，以压痕的深浅表征试样的硬度。巴柯尔硬度计（巴氏硬度计）作为 专门测量玻璃钢制品、增强或非增强硬塑料、铝及铝合金、黄铜、紫铜等较软金属硬度的专用检测工具 （ 特别 适用于玻璃钢制品 ），已被大多数国家或国际组织认可。美国材料试验协会（ ASTM ）、日本工业规范（ JIS ）、中国等国家相继制定 《用巴柯尔硬度计测量玻璃钢（ GRP ）硬度试验方法》,《纤维增强塑料巴氏（巴柯尔）硬度试验方法》GB/T3854-1983 的国家标准。因此，巴柯尔硬度计是各生产单位、计量部门在质量认证、质量监控、计量测试等方面首选的专用检测仪器。 无锡市计量科学研究所，是我国制定巴柯尔硬度检定标准的主要参与者、巴柯尔硬度最高标准器的拥有者和国产第一台巴柯尔硬度计的研制和生产单位，也是国家实验室认证的巴柯尔硬度计专业检测机构。经过二十多年的不断完善，本所生产的 H Ba 系列巴柯尔硬度计的各项性能和技术指标完全与美国 Barber-colman 公司 GYZJ 系列硬度计相媲美 。