2) sulfide precipitation
硫化沉淀
1.
Thermodynamic analysis results show that most heavy metallic ions and As(Ⅲ) in Na_2TeO_3 solution can be removed thoroughly by sulfide precipitation method.
实验确定硫化沉淀法去除杂质离子的最佳条件是:pH=11,温度为373 K,反应时间为50 min。
3) precipitated sulfur
沉淀硫黄
4) sulfate precipitate
硫酸盐沉淀
5) Precipitated barium sulfate
沉淀硫酸钡
1.
Fluidity of precipitated barium sulfate powder and its effecting factor;
沉淀硫酸钡粉体流动性及影响因素分析
2.
According to the production experience for many years,the factors of effecting on the quality of precipitated barium sulfate are summarized and the measures for improving the product quality are put forward.
根据多年的生产经验，总结出影响沉淀硫酸钡产品质量的因素；就原料液含杂质超标以及各生产工序工艺条件控制不合理提出解决问题的办法；提出了提高沉淀硫酸钡产品质量的措施。
6) ammonium sulphate precipitation
硫酸铵沉淀
1.
LDH was purified by ammonium sulphate precipitation (40% satura- tion), DEAE Sepharose F.
采用了硫酸铵沉淀、DEAESepharoseF。
2.
DCFE was purified by ammonium sulphate precipitation,CM-Sepharose fast flow ionexchange chromatography,Sephacryl S-(200.
淡豆豉浸提液经过硫酸铵沉淀、CM-Sepharose-FF离子交换色谱和Sephacryl S-200凝胶过滤等步骤,得到豆豉纤溶酶,经SDS-PAGE表明豆豉纤溶酶为单一谱带。
补充资料：沉淀硫酸钡
分子式： BaSO4
CAS号：
性质：又称沉淀硫酸钡(pre-cipitated barium sulfate)。白色斜方结晶或白色无定形粉末。密度4.50g/cm3。熔点1580℃。溶于热浓硫酸。几乎不溶于水、乙醇和稀酸。在1149℃时转变成单斜结晶。干燥时易结块。由硫化钡溶液与加入经除去钙、镁后的芒硝溶液混合，于90℃进行反应，生成沉淀，经抽滤、水洗和酸洗后，调节pH值5～6，再过滤，干燥，粉碎制得。亦可用钡黄卤与芒硝溶液反应制得。用于制造像纸和铜版纸的表面涂布剂，纺织工业的上浆剂，玻璃制品的澄清剂，油漆、油墨、塑料、橡胶填充剂，放射线的防护壁材以及用作陶瓷，搪瓷，颜料，色纸和墙纸的填料。在医疗上作消化系统造影剂。
CAS号：
性质：又称沉淀硫酸钡(pre-cipitated barium sulfate)。白色斜方结晶或白色无定形粉末。密度4.50g/cm3。熔点1580℃。溶于热浓硫酸。几乎不溶于水、乙醇和稀酸。在1149℃时转变成单斜结晶。干燥时易结块。由硫化钡溶液与加入经除去钙、镁后的芒硝溶液混合，于90℃进行反应，生成沉淀，经抽滤、水洗和酸洗后，调节pH值5～6，再过滤，干燥，粉碎制得。亦可用钡黄卤与芒硝溶液反应制得。用于制造像纸和铜版纸的表面涂布剂，纺织工业的上浆剂，玻璃制品的澄清剂，油漆、油墨、塑料、橡胶填充剂，放射线的防护壁材以及用作陶瓷，搪瓷，颜料，色纸和墙纸的填料。在医疗上作消化系统造影剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。