1) phenolic resin
酚醛树脂;防水水胶
2) water soluble phenol-formaldehyde resin
水溶性酚醛树脂
1.
Synthesis the water soluble phenol-formaldehyde resin by two step alkaline catalytic reaction;
两步碱催化法合成水溶性酚醛树脂
2.
Activated carbon prepared from water soluble phenol-formaldehyde resin for application in supercapacitor;
水溶性酚醛树脂制备超级电容器用活性炭
3.
Stability of dilute water soluble phenol-formaldehyde resin solution;
水溶性酚醛树脂稀溶液的稳定性
3) resol resins
水性酚醛树脂
1.
A high performance liquid chromatographic(HPLC) method was developed for the separation of formaldehyde and phenol from the other components of resol resins.
采用高效液相色谱法同时测定了水性酚醛树脂粘稠液体中残留的甲醛和苯酚,用2,4-二硝基苯肼对甲醛进行衍生化,然后进行色谱分离。
4) water soluble phenolic resin
水溶性酚醛树脂
1.
Weaving frictional material,soaked by water soluble phenolic resin,is tested by the DMS-1 constant speed friction and wear tester according to the standard of GB/T11834-2000.
研究了不同含碱量的水溶性酚醛树脂对摩擦材料性能的影响。
5) phenol resin wastewater
酚醛树脂废水
1.
The phenol resin wastewater contains high organic pollutants which are difficult to degrade by biology.
酚醛树脂废水中有机物浓度高，甲醛和酚类物质对生化处理细菌有强抑制和毒害作用，直接采用传统生化处理工艺无法运行，必须采用一定的预处理后才能进行生化处理。
6) phenolic resin cement
酚醛树脂水泥
补充资料：酚醛树脂
| 酚醛树脂 phenolic resins；Bakelite 酚与醛缩合聚合而成的一类合成树脂。英文缩写PF。它是一种热固性树脂，固化后是体型高分子。酚醛树脂在20世纪初研究成功，随后进行工业生产，成为第一个工业生产的合成高分子品种，并由此开创了合成高分子和塑料工业。酚醛树脂具有较好的绝缘性、耐热性、耐老化性和粘结性，制成增强塑料还显示较好的烧蚀性，价格便宜并易于生产。 酚醛树脂的酚类原料常用苯酚，以及甲酚和其他烷基取代酚、双酚A、间苯二酚等；醛类以甲醛为主，也可用多聚甲醛和其他高级醛类、糠醛等。作涂料的酚醛树脂常用植物油类、松香等天然树脂改性；作胶粘剂时常混以环氧树脂、聚乙烯醇缩醛、丁腈橡胶等改性。 当甲醛／苯酚（摩尔比）小于1时，可得热塑性产物，称热塑性酚醛树脂，即线型酚醛树脂，结构为：
式中n＜10。它不含进一步缩聚的基团，加固化剂并加热才能固化。如以六亚甲基四胺为固化剂，固化温度150 ℃，混以填料制成的模塑粉俗称电木粉。当甲醛／苯酚(摩尔比)大于1时，在碱催化下先得到甲阶段树脂，即热固型酚醛树脂，能溶于有机溶剂，结构为：
式中m＝0～2，l＝0～1，k＝0～1，n＜10。甲阶段树脂含能进一步缩聚的羟甲基，因此不需加固化剂即能固化：加热下反应得到乙阶段树脂，又称半溶酚醛树脂，不溶不熔但可溶胀和软化。再进一步反应则得到不溶不熔的体型结构丙阶段树脂，也称不溶酚醛树脂。甲阶段树脂长期存放也能自行固化。 酚醛树脂主要作为模压和层压塑料、涂料、油漆、胶粘剂，广泛应用在电子、电器、木材工业等，制成增强塑料，也作为烧蚀材料用于空间技术。酚醛树脂还可制成耐温、耐燃的纤维。 |