1) accelerated break-down test
加速破损试验
2) accelerated wear test
加速磨损试验
1.
An on-line measuring rig used in the accelerated wear test of the thrush sliding bearing was developed.
针对机械零件磨损可靠性分析的难点出发，研制出推力滑动轴承加速磨损试验在线测量机；重点报道了推力滑动轴承磨损规律的实验研究成果；提出了基于精密测量为基础的机械零件磨损可靠性计算的新理论、新方法。
2.
Experimental results demonstrated that the micron size of SiO2 particles can be applied to accelerated wear test of 3Cr13 coating.
采用该方法在MM200摩擦磨损试验机上,对高速电弧喷涂3Cr13涂层在含SiO2磨粒的润滑条件下磨损失效开展了加速磨损试验,通过对比分析扫描电镜照片筛选合适的磨粒颗粒,并分析SiO2磨粒加速涂层磨损可能的机理。
3) destructive test
破损试验
4) breakage resistance test
耐破损试验
5) Accelerated testing
加速试验
1.
METHODS According to the principles referring to the drug stability in the CHP and the standard of its quality,we carried out the stress testing,accelerated testing and long-term testing.
方法根据《中国药典》药物稳定性指导原则及乙酰谷酰胺氯化钠注射液的质量标准,对本品进行了影响因素试验、加速试验及长期试验。
2.
Accelerated life testing(ALT) and accelerated degradation testing(ADT) are two main kind of reliability accelerated testing technology.
加速寿命试验(ALT)、加速退化试验(ADT)是两种主要的加速试验技术,统计学界与可靠性工程界对加速寿命试验研究的关注较多,而对加速退化试验的相关理论研究与工程实践关注较少。
3.
Analyzing the general method of temperature screening for assembly in our country, combined with the experience of accelerated testing abroad, we proposed a definition method of parameters, such as temperature range, rate of change of temperature and dwell time.
分析了目前国内在组件温度筛选方面的一般做法,吸收国外加速试验的经验,并借鉴定量筛选中根据成效率确定无故障检验时间的方法,提出了组件温度筛选中各参数(如温度范围、温度变化速率、高低温保持时间和循环数)的确定方法,并以一种税控加油机主板的温度筛选为例,介绍了组件温度筛选方法研究中所总结的一些经验。
6) accelerated test
加速试验
1.
Effect of stray current on the dissoluble corrosion of Guangzhou metro engineering concrete by accelerated test;
杂散电流对广州地铁混凝土溶蚀性能影响的加速试验研究
2.
Method The influences of non-buffer and different buffers(phosphate buffer solution and Citrate buffer solution)on the stability of povidone-iodine gel were investigated by accelerated tests at 30 ℃and 40 ℃.
方法采用30℃和40℃加速试验考察无缓冲溶液和不同缓冲溶液(磷酸盐缓冲溶液,枸橼酸盐缓冲溶液)对聚维酮碘凝胶稳定性的影响。
3.
Methods The change of color, pH value, ingredients and the change of related materials were detected through the trials under the influence factors including sunlight, high and low temperatures and accelerated test which was done under specified conditions of constant temperatures of 40℃, 50℃, 60℃for 15 weeks as well as samples which were observed under room temperature.
方法通过光照、高温、低温等影响因素试验,特定条件(40,50,60℃)下恒温15周加速试验及室温留样观察,测定其色泽、pH、含量、有关物质变化。
补充资料：磨损试验
测定材料抵抗磨损能力的一种材料试验。通过这种试验可以比较材料的耐磨性优劣。磨损试验比常规的材料试验要复杂。首先需要考虑零部件的具体工作条件并确定磨损形式，然后选定合适的试验方法，以便使试验结果与实际结果较为吻合。
磨损形式有磨料磨损、粘着磨损、接触疲劳磨损、微动磨损、气蚀等。然而在实际运转条件下往往不止出现一种磨损形式，例如大功率柴油机轴瓦可能同时出现粘着磨损和气蚀。与其他试验相比，磨损试验受载荷、速度、温度、周围介质、表面粗糙度、润滑和偶合材料等因素的影响更大。试验条件应尽可能与实际条件一致,才能保证试验结果的可靠性。
磨损试验种类 磨损试验分为现场磨损试验和实验室磨损试验。现场磨损试验是将做成零件的试样装在机器上，在实际运转条件下进行试验。而实验室磨损试验是在实验室中的磨损试验机上进行，它又分为试样磨损试验和台架磨损试验。①试样磨损试验：用加工成一定形状和尺寸的试样进行试验。②台架磨损试验：用零件或近似零件的试样在模拟实际运转条件的台架上进行试验。
磨损试验机 按运动方式可分为滑动和滚动两类。按介质不同可分为干摩擦、有润滑、有磨料的3类。按试样接触形式（见图）可分为5类:①平面与平面；②平面与圆柱；③圆柱与圆柱；④平面与球；⑤球与球等。磨损试验机还按相对运动方向分为单方向运动和往复运动两类，也可按摩擦轨迹分为新生面摩擦和重复摩擦两种不同型式。
磨损量测量 磨损量可用试验前后的试样长度、体积、重量等的变化来表示。磨损量测量的方法有：测长法、测重法、人工基准法（刻痕法、压痕法、磨痕法）、化学分析法和放射性同位素法等。磨损试验时，经常指定某材料作为对比材料，然后在同样条件下将被测材料与它进行对比试验。试验结果用相对耐磨性系数或磨损系数表示。
磨损系数则为相对耐磨性系数的倒数。
磨损形式有磨料磨损、粘着磨损、接触疲劳磨损、微动磨损、气蚀等。然而在实际运转条件下往往不止出现一种磨损形式，例如大功率柴油机轴瓦可能同时出现粘着磨损和气蚀。与其他试验相比，磨损试验受载荷、速度、温度、周围介质、表面粗糙度、润滑和偶合材料等因素的影响更大。试验条件应尽可能与实际条件一致,才能保证试验结果的可靠性。
磨损试验种类 磨损试验分为现场磨损试验和实验室磨损试验。现场磨损试验是将做成零件的试样装在机器上，在实际运转条件下进行试验。而实验室磨损试验是在实验室中的磨损试验机上进行，它又分为试样磨损试验和台架磨损试验。①试样磨损试验：用加工成一定形状和尺寸的试样进行试验。②台架磨损试验：用零件或近似零件的试样在模拟实际运转条件的台架上进行试验。
磨损试验机 按运动方式可分为滑动和滚动两类。按介质不同可分为干摩擦、有润滑、有磨料的3类。按试样接触形式（见图）可分为5类:①平面与平面；②平面与圆柱；③圆柱与圆柱；④平面与球；⑤球与球等。磨损试验机还按相对运动方向分为单方向运动和往复运动两类，也可按摩擦轨迹分为新生面摩擦和重复摩擦两种不同型式。
磨损量测量 磨损量可用试验前后的试样长度、体积、重量等的变化来表示。磨损量测量的方法有：测长法、测重法、人工基准法（刻痕法、压痕法、磨痕法）、化学分析法和放射性同位素法等。磨损试验时，经常指定某材料作为对比材料，然后在同样条件下将被测材料与它进行对比试验。试验结果用相对耐磨性系数或磨损系数表示。
磨损系数则为相对耐磨性系数的倒数。