1) temperature compensation alloy
温度补偿合金
2) magnetic temperature compensation alloy
磁温度补偿合金
1.
Effect of heat treatment on thermal magnetic performances and microstructure of Fe_(69.07)Ni_(29.25)Mn_(0.615)Si_(0.50)C_(0.50)magnetic temperature compensation alloy;
热处理对Fe_(69.07)Ni_(29.25)Mn_(0.615)Si_(0.50)C_(0.50)磁温度补偿合金热磁性能和微观结构的影响
2.
Characterization of temperature stability of permanent magnet with magnetic temperature compensation alloy was discussed.
讨论了磁温度补偿合金与永磁体组合后的磁性能和温度稳定性的表征。
3.
Influence of forge technique on the performance of Fe-Ni magnetic temperature compensation alloy was studied by optical microscopy and magnetic property test.
采用光学显微镜、静态冲击法磁性能测试设备等研究了锻造工艺对铁镍磁温度补偿合金饱和磁感应强度Bm和磁温度系数△B/△T0-100℃的影响规律。
3) temperature compensation alloy
温度补偿用合金
4) thermoperm alloy
温差磁补偿合金
5) temperature-compensated combination
温度补偿组合
6) temperature compensation
温度补偿
1.
The method of temperature compensation in the measuring concentration of lye in mercerizing process;
丝光机碱液浓度检测温度补偿方法的研究
2.
Research and application on the siemens 840D CNC system temperature compensation function;
西门子840 D系统温度补偿功能在数控机床上的开发应用
3.
Pressure sensor temperature compensation based on least squares support vector machine;
基于最小二乘支持向量机的压力传感器温度补偿
补充资料：热磁补偿合金
一类居里点接近室温、在特定温度范围内磁感应强度(B)或磁导率(μ)随温度的升高而急剧下降的软磁合金，简称热磁合金。主要用于制作永磁器件的温度补偿元件、热敏开关元件等。1928年库斯曼(A.Z.Kussmann)报道蒙乃尔(Monel)合金的磁感在居里温度附近随温度变化而急剧变化。同时在德国出现Ni-Cu-Fe系Calmalloy型合金，1930年金纳德 (I.F.Kinnard)将该型合金应用于自补偿温度指示器。1934年施特布莱因（F.Stblein）报道了30Ni-Fe系Thermoperm合金的磁感-磁场热磁补偿的温度特性。此后热磁补偿合金发展成不同系列。中国在50年代开始少量生产热磁合金，60年代末形成合金系列。两种常用的热磁合金的磁导率随温度变化的曲线见图。
热磁合金大部为厚0.2～3mm板、带材，加工工艺与一般铁镍系软磁合金的带材工艺相似，也有一部分热磁合金采用粉末冶金、铸造或多层复合等工艺。
热磁合金大部为厚0.2～3mm板、带材，加工工艺与一般铁镍系软磁合金的带材工艺相似，也有一部分热磁合金采用粉末冶金、铸造或多层复合等工艺。