1) hydrogen bonding
氢结合
3) hydrogen-desorption-recombination
脱氢再结合
4) desorption-recombination
脱氢-再结合
1.
As-cast Nd12Fe82B6 alloy was disproportionated by mechanical milling in hydrogen atmosphere at ambient temperature, and nanocrystalline alloy powder were obtained by subsequent desorption-recombination treatment following mechanical milling.
在氢气氛中机械球磨铸态Nd12Fe82B6(at%)合金,利用机械力驱动使之发生歧化反应,随后进行真空脱氢-再结合处理,获得纳米晶合金粉末材料。
2.
As-cast Nd12Fe82B6 alloy was disproportionated by mechanical nulling in hydrogen atmosphere at ambient temperature, and nanocrystalline alloy powders were obtained by subsequent desorption-recombination treatment following mechanical milling.
在氢气氛下机械球磨铸态Nd12Fe82B6(原子比)合金,利用机械力驱动使之发生歧化反应,随后进行真空脱氢-再结合处理,获得纳米晶合金粉末材料。
3.
Nd8Fe86B6 alloy powders were mechanically milled in hydrogen atmosphere, and nanocomposite Nd2Fe14B/a-Fe magnetic material was prepared by mechanically activated disproportionation of Nd-Fe-B alloy and a subsequent desorption-recombination vacuum annealing treatment were experimentally investigated in this paper.
研究了在氢气氛下机械球磨铸态Nd8Fe86B6合金,利用机械力驱动Nd-Fe-B合金发生歧化反应,并随后在一定温度及真空度下进行脱氢-再结合处理,制备纳米晶Nd2Fe14B/a-Fe复相材料。
5) solvent hydrogen bonding
溶剂氢结合
6) Hydrogen bonding energy
氢键结合能
补充资料：氢键
| 氢键 hydrogen bond 一个与电负性高的原子X共价结合的氢原子（X—H）带有部分正电荷，能再与另一个电负性高的原子（如Y）结合，形成一个聚集体X—H…Y的化学结合作用。X、Y原子的电负性越大、半径越小，则形成的氢键越强。例如，F—H…F是最强的氢键。氢键表面上有饱和性和方向性：一个H原子只能与两个其他原子结合，X—H…Y要尽可能成直线。但氢键H…Y之间的作用主要是离子性的，呈现的方向性和饱和性主要是由 X和Y之间的库仑斥力决定的。氢键可以在分子内形成，称为内氢键；也可以在两个分子之间形成。分子间的氢键可使很多分子结合起来，形成链状、环状 、层状或立体的网络结构。 氢键的键能比较小，通常只有17～25千焦／摩尔。但氢键的形成对物质的性质有显著影响 ，例如使熔点和沸点升高；溶质与溶剂之间形成氢键，使溶解度增大 ；在核磁共振谱中氢键使有关质子的化学位移移向低场；在红外光谱中氢键X—H…Y的形成使X—H的特征振动频率变小并伴有带的加宽和强度的增加 ；氢键的形成决定蛋白质分子的构象，在生物体中起重要的作用。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。