1) off-hand working
自由成形法
2) free forming
自由成形
1.
After field analysis and investigations,we try to change the weld technique from the pad-added single sided weld with double sided formation into the free forming single sided weld with double sided formation,and we formulate the relevant welding specifications.
经过现场分析和调研,将加垫板的单面焊双面成形焊接工艺改为自由成形的单面焊双面成形焊接工艺,同时制定了相应的焊接规范。
2.
To satisfy the need of sub-sea pipeline all-position welding repair,free forming features of 16Mn steel plate in typical positions under 0.
7 MPa空气压力下,研究典型位置16 Mn钢板的自由成形,形成的接头符合美国焊接学会AWS D 3。
3) shape formation free energy
成形自由能
1.
It is found that the allowed shape of TCNTs should be determined by a restraint of shape formation free energy being equal to zero.
发现弯曲纳米碳管成形自由能为零的条件决定了多壁纳米碳管环的形成;并存在使直纳米碳管变弯的阈值条件,纳米碳管环是诸多弯曲构型中的一种稳定构型。
4) the Gibbs free energy of formation
形成自由能
6) self forming method
自成形法
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。